Investigation of MOF-derived humidity-proof hierarchical porous carbon frameworks as highly-selective toluene absorbents and sensing materials
Zehui Li,Yi Yuan,Hao Wu,Xinghui Li,Menglei Yuan,Huaizhang Wang,Xiaoxue Wu,Shuai Liu,Xianming Zheng,Mingjun Kim,Haoyun Zheng,Sadia Rehman,Guangya Jiang,Wangyang Fu,Jingkun Jiang
DOI: https://doi.org/10.1016/j.jhazmat.2020.125034
IF: 13.6
2021-06-01
Journal of Hazardous Materials
Abstract:<p>Carbon frameworks (CFs) derived from metal-organic frameworks (MOFs) have been produced as adsorbents of toluene. To further obtain optimum hierarchical porous carbon structure of CFs, different treatment temperatures were applied to a typical kind of MOFs (ZIF-8). The adsorption capacity of the toluene of hierarchical porous CFs obtained from ZIF-8 under 1100 °C (CF-1100, adsorption capacity of 208.5 mg/g) was higher than that of other carbonization temperature and MOFs. Impressively, the adsorbent CF-1100 also exhibited strong hydrophobicity, low desorption temperature, and good selectivity to toluene. The adsorption capacity decreased by only 10.4% under wet condition compared with the dry condition, standing on the top of the recently reported adsorbents. The impressive adsorption performance of CF-1100 is attributed to the larger specific surface area (1024 m<sup>2</sup>/g) and pore volume (0.497 cm<sup>3</sup>/g), newly generated micropores (pore width is 0.6~0.8 nm) and mesopores (pore width above 10 nm), and carbonaceous structure with higher degree of graphitization. Based on the adequate adsorption performance, CF-1100 coated quartz crystal microbalances as sensor also showed a high sensitivity of 0.4004 Hz/ppm and small relative standard deviations of 1.0745% for toluene sensing. This contribution provides a foundation for optimizing potential adsorbents and sensing materials for air pollution abatement.</p>
environmental sciences,engineering, environmental