Abstract:In metal-based additive manufacturing, laser power, scanning speed, hatching distance and layer thickness are important manufacturing parameters. These parameters are very important in terms of microstructure, mechanical properties and surface quality of the final product. For this reason, it is very important choosing these parameters correctly in the production process. One of the common approaches used to optimize these parameters is volumetric energy density. In this study, product quality improvement in additive manufacturing of AlSi10Mg alloy was focused, and test pieces were produced at different volumetric energy densities. The parts were manufactured according to the Taguchi L 9 orthogonal array experimental design. Three different laser powers (250–300–350 W), three different scanning speeds (900–1000–1100 mm/s), three different hatching distances (0.17–0.19–0.21 mm) and constant layer thickness values were used as manufacturing parameters. The performance properties of the manufactured parts were investigated in terms of mechanical properties and surface roughness. As a result of the study, it was observed that the mechanical properties of the samples produced at very high and very low volumetric energy densities decreased and the surface roughness increased. Maximum mechanical properties within the produced samples were obtained at 55.82 J/mm 3 volumetric energy density, and minimum surface roughness was obtained at 54.46 J/mm 3 volumetric energy density. For mechanical properties and surface roughness, multiple response optimization was performed with Taguchi-based Grey relational analysis method. According to the experimental results, optimum manufacturing parameters for additive manufacturing of AlSi10Mg alloy; it was obtained as 350 W laser power, 1100 mm/s scanning speed, 0.19 mm hatching distance and 55.82 J/mm 3 volumetric energy density, which is the interaction of these parameters. The mechanical properties and surface roughness obtained graphically were supported by fracture surface images and microstructure studies. With multiple response optimization, 30.15% improvement was achieved in performance indicators. In addition, it has been demonstrated that volumetric energy density can be used as an important evaluation tool in determining product quality.

Post-process drilling of AlSi10Mg parts by laser powder bed fusion

Investigating drilling efficiency: a study on indexable centerless drilling of Ti-6Al-4 V alloy

Experimental Investigation on Machinability of DMLS Ti6Al4V under Dry Drilling Process

Effect of Material Microstructure on Tool Wear Behavior During Machining Additively Manufactured Ti6Al4V

Drilling performance of micro-textured twist drill bit for TI-6AL-4V alloy: Validated FEM and statistical approaches

Machining Characteristics During Short Hole Drilling of Titanium Alloy Ti10V2Fe3Al

The influence of tool quality on the machining of additive manufactured and powder metallurgy titanium alloys

Fabrication of Electron Beam Melted Titanium Aluminide: The Effects of Machining Parameters and Heat Treatment on Surface Roughness and Hardness

Evaluation of the drilling process in 6061-T6 Al-Mg-Si alloys using AISI M-35 diamond-like carbon coated high-speed steel drill

Dynamic Mechanical Properties and Machinability Characteristics of Selective Laser Melted and Forged Ti6Al4V

Hole quality and tool wear when dry drilling of a new developed metal/composite co-cured material

Selective Laser Melting Process Optimization and Mechanical Properties Evolution of AlSi10Mg by Determining Temperature of the Build Chamber using Arduino IDE and Coding Algorithm

Microstructure and mechanical properties of an additively manufactured AlSi10Mg based alloy

Comparative study on MQL milling and hole making processes for laser beam powder bed fusion (L-PBF) of Ti-6Al-4V titanium alloy

High Speed EDM and Laser Drilling of Aerospace Alloys

Microstructure and tensile properties of droplet-on-demand additively manufactured AlSi7Mg

Experimental Investigation of the Micro-Milling of Additively Manufactured Titanium Alloys: Selective Laser Melting and Wrought Ti6Al4V

Experimental and statistical investigation of mechanical properties and surface roughness in additive manufacturing with selective laser melting of AlSi10Mg alloy

Influence of Abrasive Materials in Fluidised Bed Machining of AlSi10Mg Parts Made through Selective Laser Melting Technology

Drilling Process in γ-TiAl Intermetallic Alloys

Effects of Laser Processing Parameters on Microstructure and Mechanical Properties of Additively Manufactured AlSi10Mg Alloys Reinforced by TiC