Abstract:In this work, we have designed unique poly(lactic acid-co-glycolic acid)-b-poly(ethylene oxide)-b-poly(propylene oxide)-b-poly(ethylene oxide)-b-poly(lactic acid-co-glycolic acid) pentablock copolymers using Pluronic F68 and F108 triblock copolymers as macroinitiators. The poly(lactic acid-co-glycolic acid) (PLGA) blocks were attached as glycolide and lactide monomers at the both ends of each F68 and F108 triblock copolymer. The molecular weights and the block fractions were confirmed by gel permeation chromatography (GPC) and proton nuclear magnetic resonance (1H NMR) for the four kinds of pentablock copolymers. Using these pentablock copolymers as templates, we synthesized mesoporous ethane-silicas as well as silicas by the evaporation-induced self-assembly (EISA) method. 1,2-bis(triethoxysily)ethane (BTEE) were used as an organosilica precursor. The mesoporous ethane-silica samples were characterized using synchrotron small angle X-ray scattering (SAXS), nitrogen sorption experiments, transmission electron microscopy (TEM), and solid-state 29Si CP-MAS NMR. Based on the experimental results, it was confirmed that the porosity and pore diameter can be varied with the PLGA weight fraction of the pentablock copolymer. It is due to the PLGA block in polymer forming the hydrophobic domain in micelles, which leads to the formation of increased pore size over 20 nm without any additive pore expander. In addition, it seems that as the organosilica precursor increases, the association number of block copolymers forming one micelle decreases, resulting in a decrease in pore size. In , the polymer template plays a vital part in tuning the structure of the mesoporous ethane-silica samples. Thus, the development of synthetic method of mesoporous organosilica materials using polymer templates with different topology is still challenging and can endow the unique structure and property for mesoporous organosilica for future applications.

Utilization of Cage Germoxanes as Templates for Tuning Pore Characteristics of Siloxane-Based Materials

Hexagonal Prismatic Siloxanes Functionalized with Organosilyl Groups as Building Blocks of Nanoporous Materials

Direct cross-linking of silyl-functionalized cage siloxanes via nonhydrolytic siloxane bond formation for preparing nanoporous materials

Tunable Hierarchical Porous Silica Materials Using Hydrothermal Sedimentation-Aggregation Technique

Controllable Preparation Of Ultra-Low-Dielectric Nanoporous Silica Via Inorganic-Organic Hybrid Templates

Tailoring the Morphology of Monodisperse Mesoporous Silica Particles Using Different Alkoxysilanes as Silica Precursors

Building-block approach to discrete and sequence-specific oligosiloxanes

Synthesis of a series of octaalkoxy-substituted cage silsesquioxanes catalyzed by zinc acetate

Triblock Copolymer and Poly(Ethylene Glycol) As Templates for Monolithic Silica Material with Bimodal Pore Structure

Tailoring pore size of mesoporous silica and organosilica using biodegradable pentablock copolymer templates via EISA process

Silicone Surfactant Templated Mesoporous Silica

The Synthesis of Porous Materials with Macroscopically Oriented Mesopores Interconnected by Branched Mesopores

Progress on Cage Polyhedral Oligomeric Silsesquioxane

Sonochemical effect and pore structure tuning of silica xerogel by ultrasonic irradiation of semi-solid hydrogel

Pore size control of mesoporous silicas from mixtures of sodium silicate and TEOS

Tuning Material Properties of Porous Organic Cage CC3 with Postsynthetic Dynamic Covalent Chemistry

Template Synthesis of 3-D Bimodal Ordered Porous Silica

Modeling of Linear Nanopores in A-Sio2 Tuning Pore Surface Structure

Synthesis of mesoporous silica using block copolymer-cationic surfactant mixtures as templates

Synthesis and Characterization of Monovinyl-Functionalized Silsesquioxane Cage

Pore Structure Control of Macroporous Methylsilsesquioxane Monoliths Prepared by in Situ Two-Step Processing