Effects of Heat Source Angle on Weld Formation and Porosity Defects of Laser-MIG Hybrid Welding of 6A01 Aluminum Alloy
Han Xiaohui,Zhang Zhiyi,Ma Guolong,Wu Laijun,Song Xiaoguo,Wang Houqin,Tan Caiwang
DOI: https://doi.org/10.3788/CJL202249.0202020
2022-01-01
Abstract:Objective Recently, lightweight materials have been undergoing advancements and are widely used in industrial manufacturing. The use of advanced aluminum alloys in new generations of trains is a significant step to meet the increasing demand for lightweight materials. 6005A is a type of aluminum alloy used in Chinese G-series high-speed trains. The train frame is mainly composed of 6005A aluminum extrusions with a low density, high strength, and high corrosion resistance. However, the welding of 6005A aluminum alloys is difficult. Owing to the high reflectivity of aluminum alloys, laser welding usually fails. Moreover, arc welding is unsuitable for connecting aluminum alloys owing to high heat input and severe deformation occurrence. Thus, laser-MIG hybrid welding was proposed as an improved technique for welding 6005A aluminum alloys. The arc source can significantly decrease laser reflectivity and improve aluminum alloy weldability. Furthermore, the laser source can increase the processing speed and reduce the heat input. So far, most studies on the laser-MIG hybrid welding of aluminum alloys have focused on optimizing the welding processing parameters. The effects of laser power, weld current, the distance between the laser and arc, and weld speed on the welding quality have been analyzed and discussed comprehensively. However, the effects of the heat source angle on weld formation and porosity remain unclear. In this study, different heat source angles were adopted and the welding processes were compared. The influence of the heat source angle on laser-MIG hybrid weld formation and porosity defects were discussed. Methods 6005A aluminum alloy extrusions and an ER5356 welding wire were selected to perform single-pass laser-arc hybrid welding. The welding equipment was developed using a 6-kW fiber laser system (IPG YLS-6000) and a welding machine (Lincoln Power Wave R350). A laser-guided hybrid welding method was adopted. The welding processing parameters were optimized using the single factor variable method. The tensile strength and porosity defects of the welding joints with different heat source angles were tested. The electrical signals in the welding process were measured. The droplet transfer and weld pool characteristics were analyzed using high-speed cameras. Hybrid welding was simulated using Ansys 2021 software based on computational fluid dynamics methods. Results and Discussions High-quality welded joints with good appearances were obtained with different heat source angles (Figs. 1, 2, 3 and 4). When the laser source angle is 82. 5 degrees or 70 degrees, the weld depth reaches approximately 4 mm. However, when the laser source angle exceeds 90 degrees and reaches 120 degrees and 140 degrees, the weld depth decreases to 2 mm. Furthermore, the weld width decreases with increasing laser source angle (Fig. 5). The decreased weld depth improves the stability of the laser keyhole as well as contributes to the floating out of weld pores. Consequently, the porosity of the welds decreases from 3 Yo to 0 Yo when the laser source angle is varied from 82.5 degrees to 97.5 degrees (Figs. 7 and 8). Regarding the weld pool, the increased heat source angle leads to the elongation of the weld pool, which also promotes the reduction of the weld pores (Fig. 9). Simulation results, which matched with experimental results, imply that the increased laser source angle suppressed the propagation of laser power along the depth direction, thus changing the weld formation (Figs. 11 and 12). Conclusions Aluminum alloy profiles based on laser-MIG hybrid welding were studied for high-speed trains, and the influence of different heat source angles on the welding characteristics, including appearance, pores and melt flowing, was investigated. Results show that the weld depth decreases with an increase in the angle between the laser and the welding direction. When the laser source angle is increased from 82.5 degrees to 110 degrees, the penetration depth and weld width decrease by 50% and 25 %, respectively. Moreover, increasing the heat source angle is conducive for reducing the weld pores. When the laser source angle is increased from 82. 5 degrees to 97. 5 degrees, the weld porosity decreases from 3% to 0. Moreover, the droplet transfer mode was observed under different heat source angles and the length of the molten pool was promoted by increasing the angle between the laser and the welding direction. Fluent simulation results suggested that the heat source angle has significant effects on energy propagation. With an increase in the angle between the laser and the welding direction, the propagation of energy in the depth direction will decrease. The heating range increases with increasing arc angle, which is beneficial for prolonging the solidification time of molten pools and the eliminating weld pores.