Temperature Dependence of Interface Characterization and Mechanical Properties of TA1/Q235 Composite Fabricated by Explosive Welding

Cun Wang,Jianchao Han,Changjiang Zhang,Yongjun Su,Shuzhi Zhang,ZhiXiong Zhang,Tao Wang

DOI: https://doi.org/10.1002/adem.202201759

IF: 3.6

2023-02-23

Advanced Engineering Materials

Abstract:In this study, the interface characterization and tensile properties of TA1/Q235 composite fabricated by explosive welding were investigated in the temperature range 650 °C‐950 °C. The explosive welded TA1/Q235 composite presents the periodic wavy bonding interface with both the vortex region and solid‐solid bonding region. Some defects including cavities, cracks, and brittle intermetallic compounds are located in the melted zone of the interface wave. The compound layer is composed of FeTi and Fe2Ti, with a thickness of 25μm.In terms of high‐temperature tensile tests, the elongation of the TA1/Q235 composite exhibits a tendency of first increasing and then decreasing with increasing tensile temperature. And the elongation reaches the peak value of 95% at 800 °C. The tensile strength basically decreases with increasing temperature, except for a slight increase at 900 °C. The failure of the TA1/Q235 composite is affected by both the discontinuous compound layer and the continuous compound layer. With the increase in tensile temperature, a continuous compound layer with a certain thickness dominates the failure of the TA1/Q235 composite. This article is protected by copyright. All rights reserved.

materials science, multidisciplinary