Microwave-Based Synthesis of Functional Morphological Variants and Carbon Nanotube-Based Composites of VS 4 for Electrochemical Applications
Kenna L. Salvatore,Sha Tan,Christopher Tang,Joceline Gan,Matthew Licht,Cheng-Hung Lin,Xiao Tong,Yu-chen Karen Chen-Wiegart,Esther S. Takeuchi,Kenneth J. Takeuchi,Amy C. Marschilok,Stanislaus S. Wong
DOI: https://doi.org/10.1021/acssuschemeng.0c03785
2020-10-28
Abstract:A novel facile, fast, and efficient microwave-assisted method was developed to synthesize a number of diverse nanostructured motifs (ranging from nanorods to nanoflowers) of VS<sub>4</sub> along with its associated composite heterostructures, VS<sub>4</sub>/multi-walled carbon nanotube (MWNT; i.e., multi-walled carbon nanotubes). In particular, we have probed and correlated the effects of a number of specific experimental variables, including primarily precursor, solvent, temperature, and time. We noted that nanorods formed more readily with VO(acac)<sub>2</sub> as the vanadium precursor and <i>n</i>-methyl-2-pyrrolidone (NMP) as a polar reaction solvent. By contrast, we determined that hierarchical three-dimensional (3D) nanoflower-like assemblies, ranging in size from 100 to 200 nm in average diameter, could be controllably synthesized by using Na<sub>3</sub>VO<sub>4</sub> as the vanadium precursor and an aqueous water: polar solvent mixture as the reaction medium. We also observed that VS<sub>4</sub> disintegrates, when in the presence of either air, solution, or a combination of these environments, and established that the extent of VS<sub>4</sub> nanorod decomposition could be almost fully prevented by storage under nitrogen. From an application's perspective, our VS<sub>4</sub> is electrochemically active and shows behavior, consistent with the literature. In particular, as compared with pristine VS<sub>4</sub> nanorods alone, we observed enhanced electrochemical activity with (i) 3D hierarchical flower-like motifs, (ii) unique necklace-like VS<sub>4</sub> nanorod–MWNT composites, and (iii) samples in which as-prepared VS<sub>4</sub> nanorods had been annealed. Moreover, we found that the rational application of specific physical and chemical processing treatments, such as (i) thermal annealing to improve crystallinity, (ii) the addition of MWNTs to form conductive composites, and (iii) the evolution of morphology from one-dimensional (1D) nanorods to more complex 3D nanoflowers, was favorable to the resulting electrochemical performance with respect to increasing stability and reversibility.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c03785?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c03785</a>.Structural and chemical characterization results, including but not limited to XPS, XRD, SEM, SEM-EDS, and HRTEM figures, associated with analyzing the effects of various reaction parameters (including but not limited to precursors, solvents, reaction times, and reaction temperatures) on different types of as-prepared VS<sub>4</sub> motifs (including nanorods, nanoflowers, and MWNT-based composites), coupled with tables summarizing and quantifying acquired XPS and relevant storage data (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c03785/suppl_file/sc0c03785_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology