Integration of Localized Electric-Field Redistribution and Interfacial Tin Nanocoating of Lithium Microparticles toward Long-Life Lithium Metal Batteries

Minghui Ye,Wengao Zhao,Jinhao Li,Yang Yang,Yufei Zhang,Guanhua Zhang,Cheng Chao Li

DOI: https://doi.org/10.1021/acsami.0c18831

2020-12-31

Abstract:Lithium metal batteries (LMBs) have shown a huge prospect for next-generation energy storage devices, but are always plagued by the high reactivity of metallic Li and dendrite growth. Herein, we propose a strategy of localized electric field to achieve nondendritic and long-life LMBs. Li microparticles with conformal tin nanocoating () are uniformly distributed in the hollow nitrogen-doped carbon shells/graphene host, in which each works as a localized microelectric field, inducing even Li plating and stripping. Based on COMSOL simulation, the electric field relative intensity reaches the highest values at the gaps of neighboring Therefore, Li⁺ ions are preferentially plated into the gaps to achieve smooth metallic Li. Additionally the interfacial nanosized Sn–Li alloy can effectively protect against parasitic reactions <i>via</i> reducing the contact with organic solvents. Attributed to these advantages, the symmetric battery displays a low overpotential of 0.32 V at a high current density of 10 mA cm^–2 after 250 cycles. Coupled with the LiNi_0.6Co_0.2Mn_0.2O₂ layered cathode, the NCM622∥ full battery exhibits an initial discharge capacity of 171.5 mA h g^–1 at a 2 C discharge current rate and still retains 80.3% capacity after 949 cycles.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c18831?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c18831</a>.Characterization of HNCS/G, Li-MPs, and using TEM, SEM, EDS, XRD, and XPS analysis; voltage–time curves of HNCS/ foil and Cu foil during the Li plating process; characterization of Li, Li-MPs, anodes, and NCM622 cathode collected from the postcycling cells using SEM, EDS, and XPS analysis; electrochemical performances of NCM622∥Li, NCM622∥Li-MPs, and NCM622∥ cells; and comparison of electrochemical performance of different cells (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c18831/suppl_file/am0c18831_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology