Abstract:In this work, the hydrogen desorption properties of the novel Mg-Al-H hydrogen storage composites prepared by ball-milling the as-received magnesium hydride (MgH2) and the as-prepared aluminum hydride (AlH3) with different molar ratios (1:1, 1:0.5, and 1:0.25) are investigated systematically. Nonisothermal desorption measurements show that more than 7.51 wt % of hydrogen is released from the Mg-Al-H composites when they are heated from room temperature to 500 degrees C. Thermal analysis by differential scanning calorimeter (DSC) and hydrogen desorption spectrum by mass spectrometer (MS-H-2) are used synchronously to study the desorption process of the Mg-Al-H. The onset hydrogen desorption temperature of MgH2 in the MgH2 + AlH3 composite is dramatically reduced from 320 degrees C for the pure MgH2 to below 252 degrees C. The DSC/MS-H-2 and the X-ray diffraction (XRD) analyses show that the desorption of MgH2 in the Mg-Al-H composite is composed of two steps with the reaction between MgH2 and Al forming Mg17Al12 as the first step and the self-decomposition of the residual MgH2 as the second step. Isothermal desorptions show that the desorption kinetics of the MgH2 in the Mg-Al-H composite is significantly improved. The apparent activation energy for the desorption of MgH2 in the MgH2 + 0.25AlH(3) is reduced to 144.6 kJ/mol, which contributes to the improvement in the desorption kinetics of MgH2. The Johnson-Mehl-Avrami (JMA) kinetic studies indicate that the desorption kinetic model of MgH2 in the Mg-Al-H composite is different from the pure MgH2. Concerning the reversibility, under the conditions of 300 degrees C and 5 MPa H-2, MgH2 in the Mg-Al-H composite is almost fully recovered after absorption for 5 h while it is partially recovered for the pure MgH2. Among the samples studied, the MgH2 + 0.25AlH(3) composite exhibits the highest reversible hydrogen storage capacity of 6.10 wt % (H/M).

Generation of Hydrogen by the Hydrolysis of Mixtures of Magnesium Hydride with Citric Acid

Enhanced Hydrogen Generation Properties Of Mgh2-Based Hydrides By Breaking The Magnesium Hydroxide Passivation Layer

Hydrogen generation from the hydrolysis of Mg powder ball-milled with AlCl3

Hydrogen Generation from Mg–LiBH4 Hydrolysis Improved by AlCl3 Addition

Hydrogen Generation by Hydrolysis of MgH2-LiH Composite

Hydrogen Generation by Hydrolysis of Magnesium Hydride Composites with TiFe/Ti3Fe3O Additives and Graphite

Hydrogen Generation by Hydrolysis of MgH<sub>2</sub>-LiH Composite

Controllable hydrogen generation behavior by hydrolysis of MgH2-based materials

Hydrolysis of Mg-based Alloys and Their Hydrides for Efficient Hydrogen Generation

Exploration of hydrogen generation from an Mg-LiBH4 system improved by NiCl2 addition

Hydrogen desorption properties of the MgH2-AlH3 composites

Ultrafast Hydrogen Production via Hydrolysis of MgH2-NaH Composite

Hydrogen Production Via Hydrolysis of Mg-oxide Composites

Promoting Catalysis in Magnesium Hydride for Solid-State Hydrogen Storage Through Manipulating the Elements of High Entropy Oxides

Hydrogen generation behaviors from hydrolysis of cold-welding free magnesium-calcium hydride-expanded graphite composites

Magnesium Borohydride Hydrolysis with Kinetics Controlled by Ammoniate Formation

The assessment of the importance and catalytic role of chromium oxide and chromium carbide for hydrogen generation via hydrolysis of Magnesium

Enhanced hydrogen generation via hydrolysis of Mg–Mg2NiH4 system

MgH2Insights Used for Hydrogen Storage and Catalysis: Preparation, Characterization and Mechanism

Hydrogen Generation by Hydrolysis of Mg-Mg2Si Composite and Enhanced Kinetics Performance from Introducing of MgCl2 and Si

Production of Hydrogen Via Hydrolysis of Hydrides in Mg–La System