Amphiphilic Calcium Alginate Carbon Aerogels: Broad-Spectrum Adsorbents for Ionic and Solvent Dyes with Multiple Functions for Decolorized Oil–Water Separation
Xiuxiu Tian,Haishan Zhu,Xiao Meng,Jiao Wang,Chenglin Zheng,Yanzhi Xia,Zhong Xiong
DOI: https://doi.org/10.1021/acssuschemeng.0c00129
2020-08-03
Abstract:Development of versatile, broad-spectrum adsorbents for the removal of diverse dyes from contaminated water and oil is highly desirable. In this study, a calcium alginate carbon aerogel (CCA) as an adsorbent for various types of dyes was fabricated from sodium alginate by wet spinning, cross-linking, drying, and high-temperature carbonization. The CCA carbonized at 1000 °C (CCA-1000) showed a good adsorption effect on methylene blue as a cationic dye, methyl orange as an anionic dye, oil red O as a solvent dye, and nine other dyes. Adsorption kinetics, adsorption effect of various parameters such as temperature and solution pH, regeneration performance, and adsorption mechanism were studied. The ultrahigh adsorption capacities of CCA-1000 for malachite green, crystal violet, and acid fuchsin, each with similar triphenylmethane structures, were determined to be 7059, 2390, and 6964 mg g<sup>–1</sup>, respectively. Interestingly, unlike previously reported carbon aerogels with simple oil–water separation, due to the amphiphilicity, CCA-1000 fabricated herein can be utilized to separate oil–water, surfactant-stabilized water-in-oil, and oil-in-water emulsions with simultaneous dye removal from water and oil. The present work may open up a new avenue for designing carbon aerogels with exceptional performance for broad-spectrum dye adsorption and oil–water separation from sustainable natural seaweed resources.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c00129?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c00129</a>.Chemical structures of all of the dyes utilized in this study (Figure S1); TGA curve of CA (Figure S2); high-resolution O 1s and Ca 2p XPS spectra of CCA-1000 (Figure S3); high-resolution C 1s, O 1s, and Ca 2p XPS spectra of CCA-800 (Figure S4); the adsorption process of CCA-500 and CA for MB, MO, and oil red O (Figure S5); UV–vis absorptions of MB, MO, and oil red O solutions before and after decolorization after 7 h by CA, CCA-500, CCA-800, and CCA-1000 (Figure S6); peak positions and areas of CCA-800 and CCA-1000 calculated by XPS results (Table S1); kinetic parameters for the adsorption of MB, MO, and oil red O on CCA-1000 (Table S2); thermodynamic parameters for the adsorption of MB, MO, and oil red O on CCA-1000 (Table S3); the reported adsorption capacities of various adsorbents for MG, CV, and AF dye with the result of our work (Table S4) (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c00129/suppl_file/sc0c00129_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology