Research on Hot Deformation Rheological Stress of Al-Mg-Si-Mn-Sc Aluminium Alloy

Wei Sun,Yu Zhang,Fang Yu,Lingfei Yang,Dongfu Song,Guozhong He,Weiping Tong,Xiangjie Wang

DOI: https://doi.org/10.3390/ma17133159

IF: 3.4

2024-06-28

Materials

Abstract:The hot compression simulation testing machine was utilized to conduct compression experiments on an Al-Mg-Si-Mn alloy containing the rare earth element Sc at a deformation temperature ranging from 450 to 550 °C and a strain rate of 0.01 to 10 s−1. The study focused on the hot deformation behavior of the aluminum alloy, resulting in the determination of the optimal range of deformation process parameters for the alloy. The relationship between material flow stress, deformation temperature, and strain rate was described using the Arrhenius relationship containing thermal activation energy based on the stress-strain curve of hot compression deformation of aluminum alloy. This led to calculations for structural factor A, stress index n, and stress level parameters as well as thermal deformation activation energy to establish a constitutive Formula for hot deformation rheological stress of aluminum alloy and calculate the power dissipation factor η. Through this process, an optimized range for the optimal deformation process parameter for aluminum alloy was determined (deformation temperature: 490~510 °C; strain rate: 0.05 s−1) and verified in combination with mechanical properties and microstructure through hot extrusion deformation trial production.

materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter

What problem does this paper attempt to address?

This paper mainly discusses the rheological behavior of aluminum-magnesium-silicon-manganese alloy containing scandium (Sc) during hot deformation. The research objective is to determine the optimal process parameter range of this aluminum alloy in the hot working process, in order to improve the application performance of the aluminum alloy, especially in the application of lightweight technology in automotive structures.

Experiments were conducted using a hot compression simulation testing machine to compress the alloy under different strain rates (0.01 to 10 s^(-1)) and deformation temperatures (450 to 550°C), studying its hot deformation behavior. By analyzing the stress-strain curve, a constitutive equation based on the Arrhenius relationship for the thermal activation energy was established. The structural factor A, stress exponent n, stress level parameter, and thermal deformation activation energy were calculated to obtain the rheological stress equation for the aluminum alloy, as well as the power dissipation factor η.

The results showed that with the increase in temperature, the flow stress of the alloy decreased, demonstrating positive strain rate sensitivity. Based on these data, the researchers plotted a processing map and determined the optimal hot deformation process parameter range for the aluminum alloy (deformation temperature: 490-510°C; strain rate: 0.05 s^(-1)). These parameters were validated through hot extrusion deformation tests.

In addition, the paper also discusses the improvement of alloy performance by the addition of scandium, such as increased strength and elongation, as well as the research status of aluminum-magnesium-silicon alloys. It points out that research in this field is relatively limited, especially in terms of rheological stress in hot extrusion production.