Abstract:Supercapacitors with transition bimetallic oxides as pseudocapacitive materials have been of wide concern for their excellent energy storage performance. In this work, a simple coprecipitation method was used to synthesize the precursor, followed by calcination to prepare Ni-Cu bimetallic oxide materials. The structure, morphology and properties of the materials prepared by different precipitating agents and different calcination temperatures of NCO-H2C2O4 precursor were investigated. The optimum precipitant was determined to be H2C2O4, and Ni-Cu nanoparticles with regular lamellar microstructure were obtained at the calcination temperature of 400 °C. The nanostructure and morphology provide a large active channel for the rapid diffusion of electrolyte ions, and the specific capacitance of NCO-H2C2O4-400 electrode material can reach 740.31 F/g Cs at 1 A/g. The investigation of charge storage mechanism shows that the contribution rate of capacitance and diffusion control is about 37.9% and 67.2%, respectively. The electrochemical test results of the asymmetric supercapacitors (ASC) constructed with NCO-H2C2O4-400 and activated carbon show that the specific capacitance, energy density, and power density of the capacitor are 52.66 F/g, 16.45 Wh/kg, and 759.51 W/kg, respectively. Even after 5000 charge/discharge cycles at 5 A/g, it can still keep 90.57% of its initial capacity. This work not only provides competitive electrode materials for energy storage devices but also provides a feasible strategy for producing complex transition metal oxide materials with high capacitance performance.

Ultrathin α-Bi2O3 Nanosheets Prepared via Hydrothermal Method for Electrochemical Supercapacitor Applications

A Few Atoms Thick Nickel–Cobalt Oxides Mesoporous Nanosheets and Their Arrays on Ni Foam for Supercapacitors with Ultra-Long Cycling Lifespan

Ultrathin Nickel Hydroxide and Oxide Nanosheets: Synthesis, Characterizations and Excellent Supercapacitor Performances.

Synthesis of NiMn-LDH Nanosheet@Ni 3 S 2 Nanorod Hybrid Structures for Supercapacitor Electrode Materials with Ultrahigh Specific Capacitance

Ultrathin Ni(OH)2 Nanosheets: Microemulsion Assisted Hydrothermal Synthesis and Application in Advanced Hybrid Supercapacitors

Electrochemical Behaviour of Ultrasonic Probe Assisted Nickel Pyrophosphate (Ni2P2O7) Nanosheets for Supercapacitor Applications

Facile synthesis of nanostructured bismuth oxide on nickel foam with outstanding electrochemical behavior for supercapacitor application

Nickel-Copper Bimetallic Oxide Nanoparticles Prepared by Simple Coprecipitation Method as High Performance Electrode Materials for Asymmetric Supercapacitors

Facile and Environmentally Friendly Synthesis of Ultrathin Nickel Hydroxide Nanosheets with Excellent Supercapacitor Performances.

Ni-Mn Bimetallic Oxide Nanosheets As High-Performance Electrode Materials for Asymmetric Supercapacitors

Galvanic displacement assembly of ultrathin Co3O4 nanosheet arrays on nickel foam for a high-performance supercapacitor

Supercapacitor performance of porous nickel cobaltite nanosheets

Influence of Deposition Potential on Electrodeposited Bismuth‐Copper Oxide Electrodes for Asymmetric Supercapacitor

Fabrication of Cobalt-Nickel-Zinc Ternary Oxide Nanosheet and Applications for Supercapacitor Electrode

The Facile Synthesis of Hierarchical NiCoO2 Nanotubes Comprised Ultrathin Nanosheets for Supercapacitors

Facile preparation of porous sheet-sheet hierarchical nanostructure NiO/Ni-Co-Mn-O x with enhanced specific capacity and cycling stability for high performance supercapacitors

Electrochemical Performance of Bi2o2co3 Nanosheets As Negative Electrode Material for Supercapacitors

Facile synthesis of bismuth niobium oxide (Bi3NbO7) micro squares as a novel pseudocapacitive electrode material for supercapacitors

Two-dimensional porous nickel oxalate thin sheets constructed by ultrathin nanosheets as electrode materials for high-performance aqueous supercapacitors

Controllable synthesis of ZnCo2O4@NiCo2O4 hierarchical nanosheets for high performance supercapacitors

Nickel hydroxide nanosheets grown on nickel foam for high performance supercapacitor applications