Coupling Effect of Hydrostatic Pressure and Erosion on Corrosion Behavior of X70 Steel in Simulated Seawater

PengWei Ren,XingYing Tang,Zu’an Qin,YingHui Wang,Jianjun Cai

DOI: https://doi.org/10.1021/acsomega.2c05435

IF: 4.1

2022-12-14

ACS Omega

Abstract:ACS Omega . 2022 Nov 23;7(48):44033-44046. doi: 10.1021/acsomega.2c05435. eCollection 2022 Dec 6. NO

chemistry, multidisciplinary

What problem does this paper attempt to address?

Effect of hydrostatic pressure on galvanic corrosion of low-alloy steel in simulated deep-sea environments

Yuxin Wang,Fulei Yan,Bo Wu,Jianhua Wu,Kefeng Hu,Xianbin Hou,Leyang Dai

DOI: https://doi.org/10.1080/1478422X.2022.2119006

2022-09-08

Abstract:In order to study the effect of high hydrostatic pressure on the corrosion of low-alloy steels in deep-sea environments. The electrochemical corrosion behavior of single-metal system and triple-metal coupled system of 907A steel, 921A steel and 1# steel under different hydrostatic pressures were studied by electrochemical, weight loss and morphology observation methods. The results show that the high hydrostatic pressure promotes the corrosion of low-alloy steel by changing the composition and morphology of corrosion products. In addition, there was also severe galvanic corrosion between the couples with a low potential difference (< 60 mV),907A steel was used as the anode of the three-metal coupled system, and 921A steel and 1# steel as the cathode. The galvanic coupling effect accelerates the pitting corrosion of 907A steel as an anode metal. When using multi-metal couplers with low potential differences, they should be protected by both coating protection and cathodic protection.
Effect of Rotating Speed and Hydrostatic Pressure on Erosion- Corrosion Behavior of X65 Pipeline Steel

Qiongbin Zheng,Liuyan Zhang,Xiaohua Jie,Xiaoye Huang,Song Luo,

DOI: https://doi.org/10.20964/2017.03.10

IF: 1.541

2017-03-01

International Journal of Electrochemical Science

Abstract:A simple rotating experimental setup with adjustable rotating speed and hydrostatic pressure was established to simulate the erosion-corrosion environment. The effect of rotating speed and hydrostatic pressure on the erosion-corrosion behavior of X65 steel in 3.5 mass% NaCl was investigated by polarization, electrochemical impedance spectroscopy, and scanning electron microscopy. The results revealed that the rotating speed changed the corrosion type of X65 steel from a pure uniform electrochemical corrosion into the combination of uniform corrosion and local damage, which was aggravated with increasing the rotating speed. The hydrostatic pressure has the opposite effect on the uniform and local corrosion of X65 steel, showing a decrease of uniform corrosion and an increase of local damage.

electrochemistry
Corrosion behavior of the low alloy weathering steels coupled with stainless steel in simulated open atmosphere

Wenhua Zhang,Shanwu Yang,Wen-Tong Geng,Qiang Hu,Lujun Zhou

DOI: https://doi.org/10.1016/j.matchemphys.2022.126409

IF: 4.778

2022-06-21

Materials Chemistry and Physics

Abstract:The corrosion behavior of low alloy weathering steels coupled with 316 L stainless steel in simulated open marine atmosphere was investigated. It was found that under alternating of dry and wet conditions, weathering steels alternately occur galvanic corrosion and atmospheric corrosion. Galvanic corrosion, which inhibits micro-cell reaction on weathering steel, produces uniform rust layers. While atmospheric corrosion increases the compactness of rust layers due to enrichment of alloying elements. Coupling is helpful to form protective rust layers for weathering steels, which eventually leads to polarity reversal during galvanic corrosion. The Cr enhances corrosion potential, reduces corrosion rate of weathering steels.

materials science, multidisciplinary
Hydrostatic pressure effects on corrosion behaviour of X80 steel in artificial sea water

Chengcheng Xu,Yuxiang Zhu,Wanlei Liu,Feihu Bao,Erju Liu,Feifei Huang,Lei Wen,Ying Jin,Dongbai Sun

DOI: https://doi.org/10.1080/1478422X.2020.1866844

2021-01-08

Abstract:The effect of hydrostatic pressure (HP) on the corrosion behaviour of X80 steel is investigated to assist the development of deep-sea oil and gas resources. The results show that the corrosion current increases as HP increases whereas the charge transfer resistance follows the opposite trend. The corrosion products are composed of γ -FeOOH, α -Fe 2 O 3 and α -FeOOH at atmospheric pressure, while Fe 3 O 4 is only formed at a high HP. Additionally, the inner layer of the corrosion products contains more Fe 3 O 4 compared with the surface corrosion layer. HP accelerates the corrosion rate of X80 steel due to its effect on the chemical and physical properties of the corrosion products, including the promoted reduction of γ -FeOOH and the formation of wider and deeper cracks on the corrosion product layer.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Influence of Hydrostatic Pressure on the Pitting Corrosion Behavior of API X80 Steel

Chengcheng Xu,Meng Yu,Yuxiang Zhu,Ying Jin,Lei Wen,Dongbai Sun

DOI: https://doi.org/10.5006/3810

2021-10-04

CORROSION

Abstract:The effect of hydrostatic pressure on the metastable and stable pitting corrosion of API X80 steel was investigated in a simulated deep-sea environment. Cumulative probability distribution analysis of metastable pitting events revealed that hydrostatic pressure promoted the occurrence of metastable pitting corrosion and the transformation of metastable pitting corrosion to stable pitting corrosion. According to the results of scanning Kelvin probe force microscopy tests, pitting corrosion of the test steel originated at the interface between inclusions and the substrate. Combined with finite element analysis, the mechanism by which hydrostatic pressure promoted the occurrence and propagation of stable pitting corrosion of test steel in the simulated deep-sea environment was explained.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Effects of Environmental Factors on Corrosion Behavior of E690 Steel in Simulated Marine Environment

Jingjing Peng,Jing Liu,Shen Zhang,Zhihui Wang,Xian Zhang,Kaiming Wu

DOI: https://doi.org/10.1007/s40195-023-01637-1

2024-01-03

Acta Metallurgica Sinica (English Letters)

Abstract:The effects of hydrostatic pressure, dissolved oxygen, temperature and flow velocity, and their interaction on the corrosion rates of E690 high-strength steel (HSS) in simulated marine environments were studied using response surface methodology. The results show that the flow velocity exerts the most significant influence on the corrosion rate of E690 HSS. Consequently, the corrosion behavior of E690 HSS under varying flow velocities were analyzed profoundly from initial pitting corrosion to long-term corrosion properties. The results indicate that the flow state facilitates the mass transfer and enhances the adsorption tendency of Cl − by enhancing the electrochemical activity of the steel surface. These factors accelerate the electrochemical reactions, resulting in increased pitting density, depth and the long-term corrosion rates in dynamic seawater environments.

metallurgy & metallurgical engineering
Synergistic effects of fluid flow and hydrostatic pressure on the degradation of epoxy coating in the simulated deep-sea environment

Fandi Meng,Li Liu,Erhai Liu,Hongpeng Zheng,Rui Liu,Yu Cui,Fuhui Wang

DOI: https://doi.org/10.1016/j.porgcoat.2021.106449

IF: 6.6

2021-10-01

Progress in Organic Coatings

Abstract:The anticorrosion performance of epoxy varnish coating/steel systems under a simulated deep-sea fluid-pressure (FP) environment was studied using physical performance tests, electrochemical measurements and finite element modeling. The results show that fluid flow provides an initial kinetic energy to water, and the hydrostatic pressure difference reduces the energy barrier for water absorption, leading to premature corrosion of the coated steel under FP condition. Detachment of polymer pieces from the coating surface and large areas of blistering are found to occur under the synergistic effects of fluid and pressure, which can be attributed to the release of internal stress at coating defects.

materials science, coatings & films,chemistry, applied
Effect of cathodic polarizations on the failure behavior of epoxy coating/low alloy steel systems under high hydrostatic pressure

Hui Guo,Jiyuan Ma,Kun Zhou,Xinyue Zhang,Yuzhu Li,Bo Fang,Zhenliang Feng,Kunshan Xu,Jie Liu

DOI: https://doi.org/10.1016/j.jmrt.2024.05.146

IF: 6.267

2024-05-27

Journal of Materials Research and Technology

Abstract:Failure behavior of epoxy coating/low alloy steel systems applied with cathodic polarization at 0.1 MPa and 15 MPa was investigated based on a deep−sea environment simulation test device. The results showed that the diffusion of water into the coating was significantly accelerated by the high hydrostatic pressure under the same polarization potential, and the time of water uptake of the coating that reached saturation was shortened; the coating's physical structure was significantly affected by the high hydrostatic pressure; the generation of highly conductive Fe 3 O 4 was promoted in the corrosion products, which accelerated the metal corrosion process. Under the same hydrostatic pressure, with the negative shift of the polarization potential, the coating protective performance was significantly reduced and metal corrosion was mitigated to a certain extent; the water transport behavior showed a tendency to shorten the time of water uptake of the coating that reached saturation and lengthen the duration of the saturation state, which may be related to a more severe degree of cathodic delamination and the increase of water consumption for cathodic reactions under the coating. In addition, the increase of the weakly conductive α−Fe 2 O 3 content in the corrosion products may cause a reduction in the cathodic protection current at the same polarization potential, resulting in the reduction of the protection effect on the metal.

materials science, multidisciplinary,metallurgy & metallurgical engineering
A Statistical Study on the Effect of Hydrostatic Pressure on Metastable Pitting Corrosion of X70 Pipeline Steel

Zixuan Yang,Bo Kan,Jinxu Li,Yanjing Su,Lijie Qiao,Alex A. Volinsky

DOI: https://doi.org/10.3390/ma10111307

IF: 3.4

2017-11-14

Materials

Abstract:Hydrostatic pressure effects on pitting initiation and propagation in X70 steel are investigated by evaluating metastable pitting probability using electrochemical methods and immersion corrosion tests in containing chlorine ion solution. Potentiodynamic tests indicated that hydrostatic pressure can decrease the breakdown potential and lead to a reduced transpassivity region. Metastable test results revealed that hydrostatic pressure can increase metastable pitting formation frequency and promote stabilization of metastable pitting growth. Electrochemical impedance spectroscopy (EIS) results indicate that Hydrostatic pressure decreases the charge transfer resistance and increases the dissolution rate within the cavities. Corrosion test results also indicated that pitting initiation and propagation are accelerated by hydrostatic pressure. Result validity was verified by evaluating metastable pitting to predict pitting corrosion resistance.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
Effect of Hydrogen Charging on the Stress Corrosion Cracking Behavior of X70 Steel in Simulated Deep Seawater Environment

Xiaojia Yang,Feilong Sun,Qing Li,Renzheng Zhu,Zhiyong Liu,Cuiwei Du,Xiaogang Li

DOI: https://doi.org/10.3390/met12020334

IF: 2.695

2022-02-14

Metals

Abstract:The effects of hydrogen charging on the electrochemical and stress corrosion cracking (SCC) behavior of X70 steel in a simulated deep seawater environment were investigated by using electrochemical measurements, slow strain rate tensile (SSRT) tests, and corrosion morphology characterization through SEM. The results showed that the concentrations of the adsorbed hydrogen in X70 steel after precharging under different hydrostatic pressures increased gradually and tended to be steady with the charging time. High hydrostatic pressures promoted the hydrogen permeation of X70 pipeline steel by promoting the permeating rate and quantity. The SCC susceptibility of X70 steel decreased first and then increased with the hydrogen-charging current density. The area reduction loss (Iψ) and true strain loss (Iε) exhibited the lowest SCC susceptibility at the 25 mA/cm2 hydrogen-precharging current density. The elongation rate loss (Iδ) exhibited the lowest SCC susceptibility at the 50 mA/cm2 hydrogen-precharging current density.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Impact of Multi-Factor Coupling on the Corrosion Behavior of 254smo Stainless Steel in an Aggressive Oilfield Environment Containing Co2 and H2s

Yang Zhao,Kai Xi,Penghui Yue,Bo He,Shucai Zhang,Huabing Li,Tao Zhang,Fuhui Wang

DOI: https://doi.org/10.1016/j.corsci.2024.112215

IF: 7.72

2024-01-01

Corrosion Science

Abstract:The passivity and corrosion behavior of 254SMo stainless steel in aggressive oilfield environments containing both carbon dioxide (CO2) and hydrogen sulfide (H2S) were investigated using weight-loss and surface analyses. The results indicated that the corrosion rate increased with the increase in temperature, CO2/H2S partial pressures, tensile stress and flow rate. Compressive stress led to a reduction in sulfide compound contents and promoted the formation of protective oxide films, while tensile stress had an opposite effect. Furthermore, a synergistic effect of stress and flow was observed.
Electrochemical corrosion behavior of high strength steel in simulated deep-sea environment under different hydrostatic pressure

Wenshan Peng,Tigang Duan,Jian Hou,Xianglong Guo,Yunhao Zhang,Li Ma,Mingdong Yu,Yonglei Xin,Shaohua Xing,Haibing Zhang

DOI: https://doi.org/10.1016/j.jmrt.2023.01.130

IF: 6.267

2023-01-26

Journal of Materials Research and Technology

Abstract:The corrosion behavior of Ni-Cr-Mo-V high strength steel in the simulated deep-sea environment under different hydrostatic pressure and immersion time is investigated using electrochemical techniques, microscopic morphology observation and Raman spectrometer. During the first 10 days immersion, the corrosion rate presents wave-like changes. The corrosion rate under different hydrostatic pressure tends to be stable after 10 days immersion. The area with uneven composition will preferentially dissolve and form corrosion pits. The local corrosion takes the corrosion pit as the center, expands and fuses around, and finally forms uniform corrosion. High hydrostatic pressure promotes β-FeOOH transforming into other corrosion products. The anode of the steel tends to active dissolution and the cathode show oxygen diffusion control characteristics at the initial stage of corrosion. Under 20 MPa, step-shape passivation appears in the anode region. Due to the rapid reaction, the corrosion product film has poor protection performance and dissolves, which resulting in not obvious passivation phenomenon.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Corrosion form transition of mooring chain steel in simulated deep-sea environments: remarkable roles of dissolved oxygen and hydrostatic pressure

Xuewei Zhang,Weijie Wu,Yuan Li,Jinxu Li,Lijie Qiao

DOI: https://doi.org/10.1016/j.jmst.2023.04.013

IF: 10.319

2023-05-21

Journal of Materials Science and Technology

Abstract:The corrosion form and mechanical properties deterioration of mooring chain steel in simulated deep-sea environments were investigated. With the increase of ocean depth, not only the pressure increases, but also the dissolved oxygen content decreases. These two factors affect corrosion evolution of mooring chain steel in simulated deep-sea environments, which was studied for the first time. Compared with uniform corrosion of mooring chain steel in shallow sea with sufficient oxygen, low dissolved oxygen leads to the corrosion dominated by pitting with pit covers. Meanwhile, hydrostatic pressure distinctly accelerates pitting initiation and propagation. The higher the hydrostatic pressure is, the more serious the pitting is. For failure mechanism of unstressed mooring chain steel serving in simulated deep-sea environments, both absorbed hydrogen and corrosion morphology can degrade the ductility of mooring chain steel, in which the leading factor depends on the service time. The severe pitting is the main factor and causes remarkable ductility loss of the steel after long-term immersion. But hydrogen plays an important role on elongation loss in early stage. Graphical abstract Download : Download high-res image (318KB) Download : Download full-size image
Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Pan Liu,Lulu Hu,Xuyang Zhao,Qinhao Zhang,Zuosi Yu,Jiming Hu,Yiqing Chen,Fangfang Wu,Fahe Cao

DOI: https://doi.org/10.1016/j.corsci.2020.108686

IF: 7.72

2020-01-01

Corrosion Science

Abstract:The microstructure and corrosion behavior of weathering steel in three solutions (S1: 3.5 wt.% NaCl, S2: 3.5 wt. % NaCl+0.052 wt.% NaHSO3, S3: 3.5 wt.% NaCl+0.907 wt.% NaHCO3) were investigated. A high proportion of random boundaries is responsible for strong corrosion sensitivity. The thickness of rust increases with immersion time and is in the order of S1>S3>S2. The rust formed in S1 and S2 solutions mainly consists of gamma-FeOOH phase, but the latter is less protective. The rust formed in S1 solution is dense and thick resulting in its protection being similar to that in S3 solution.
Tribocorrosion of 316L stainless steel by in-situ electrochemical methods under deep-sea high hydrostatic pressure environment

Pengwei Ren,Huimin Meng,Qijun Xia,Zhongzheng Zhu,Mingtao He

DOI: https://doi.org/10.1016/j.corsci.2022.110315

IF: 7.72

2022-04-01

Corrosion Science

Abstract:In-depth understanding of tribocorrosion of 316L SS in deep-sea is important for deep-sea application. In this work, the tribocorrosion behaviors of 316L stainless steel in 3.5 wt.% NaCl solution at different hydrostatic pressures have been investigated by in-situ electrochemical means. The results showed that tribocorrosion rate increased with hydrostatic pressure at a rate of 8.96 × 10−6 mm3·N−1·m−1·MPa−1. The passive film at higher hydrostatic pressure had lower OH and higher Cl-, which deteriorated the pitting susceptibility resistance. Consequently, the tribocorrosion volume increased due to the larger mechanical wear and enhanced synergism by corrosion-accelerated wear at higher hydrostatic pressure in deep-sea.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Erosion–corrosion behavior of X65 carbon steel in oilfield formation water

Jingbo Liu,Jihui Wang,Wenbin Hu,

DOI: https://doi.org/10.20964/2019.01.51

IF: 1.541

2019-01-01

International Journal of Electrochemical Science

Abstract:Erosion–corrosion behavior of an X65 steel reducer in oilfield formation water containing quartz sand particles was investigated using circulating loop system and scanning electron microscopy (SEM). The corrosion behavior of the X65 reducer during the erosion–corrosion was determined by electrochemical impedance spectroscopy (EIS), and the erosion behavior of the X65 reducer was simulated and calculated via computational fluid dynamic (CFD) method. By the synergistic interaction between erosion and corrosion, the pure corrosion rate, pure erosion rate, corrosion-enhanced erosion rate and erosion-enhanced corrosion rate of the typical reducer locations in the erosion–corrosion rate were quantified and compared. The experimental and simulation results indicated that with the decreasing of tube diameter the erosion–corrosion rate, erosion rate (total erosion rate, pure erosion rate and corrosion-enhanced erosion rate) and their percentages in erosion–corrosion rate are increased. And the total corrosion rate and erosion-enhanced corrosion rate are also increased with the decreasing of tube diameter, but their percentages in erosion–corrosion rate are reduced. From the location of tube top, tube side to the tube bottom, a similar erosion–corrosion behavior could be obtained except for the reduction of corrosion-enhanced erosion rate and its percentage in erosion–corrosion rate. This erosion–corrosion behavior of the reducer is result from the distribution of flow velocity and sand particle concentration and the synergistic interaction between erosion and corrosion, especially the erosion-enhanced corrosion behavior.

electrochemistry
Synergistic effect between fluid flow and hydrostatic pressure on the failure behaviour of epoxy coating under deep ocean hydrodynamic environment

Fu-hui Wang,Li Liu,F. Meng,Y. Cui

Abstract:Organic coating is an effective means for the corrosion protection of marine metallic materials. Nevertheless, for the coatings applied in deep-sea environment, the coating deterioration tends to occur prematurely. Deep ocean environment is complex, with a number of factors affecting the corrosion process of the steel and the failure behaviour of coatings. In particular, for some machinery and equipment moving in the deep ocean, the fluid hydrodynamics accompanied by hydrostatic pressure play significant roles through a complicated interrelationship. However, seldom literatures have been reported on the failure of coatings under such fluid-pressure (FP) condition, which is closer to the real service environment. It is still uncertain the variations of protective performance and failure behaviour of organic coatings under FP condition, and how the interaction between fluid and pressure works to accelerate the coating degradation.

Environmental Science,Engineering,Materials Science
Coupling Effects of pH and Dissolved Oxygen on the Corrosion Behavior and Mechanism of X80 Steel in Acidic Soil Simulated Solution

Shuaixing Wang,Xiaole Yin,Hao Zhang,Daoxin Liu,Nan Du

DOI: https://doi.org/10.3390/ma12193175

2019-09-27

Abstract:In an acidic red soil environment, the corrosion mechanism of X80 steel may be closely related to the pH value and oxygen content, but it has not yet formed a systematic understanding. In this paper, the coupling effects of pH and dissolved oxygen on the corrosion behavior and mechanism of X80 steel in an acidic soil simulated solution were further analyzed by electrochemical methods and three-dimensional video microscope. Results showed that the hydrogen reduction reaction was almost the only cathode process in the anoxic and low pH system, and small and dense pits were present on the electrode surface. pH value increased, the pits decreased, but the size of pits increased. In the oxygen-adequate system, oxygen-consuming (OC) corrosion preferentially occurred, and a protective corrosion product layer (including FeOOH, Fe3O4, etc.) might be formed accordingly, but the proportion of hydrogen evolution (HE) increased and the product layer had defects at a low pH environment. The specific corrosion mechanism of X80 steel in an acidic soil simulated solution is described in the relevant models.
Erosion–Corrosion Behavior of Friction Stud Welded Joints of X65 Pipelines in Simulated Seawater under Different Flow Rates

Jie Zhao,Yuqi Feng,Hui Gao,Lei Wang,Xiaoyu Yang,Yanhong Gu

DOI: https://doi.org/10.3390/ma16124326

IF: 3.4

2023-06-12

Materials

Abstract:In order to study the complex erosion–corrosion mechanism of friction stud welded joints in seawater, experiments were carried out in the mixed solution of 3 wt% sea sand and 3.5% NaCl at flow rates of 0 m/s, 0.2 m/s, 0.4 m/s, and 0.6 m/s. The effects of corrosion and erosion–corrosion at different flow rates on materials were compared. The corrosion resistance of X65 friction stud welded joint was studied by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PDP) curves. The corrosion morphology was observed by a scanning electron microscope (SEM), and the corrosion products were analyzed by energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results showed that the corrosion current density decreased first and then increased with the increase in the simulated seawater flow rate, which indicated that the corrosion resistance of the friction stud welded joint increased first and then decreased. The corrosion products are FeOOH (α-FeOOH and γ-FeOOH), and Fe3O4. According to the experimental results, the erosion–corrosion mechanism of friction stud welded joints in seawater environment was predicted.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
Corrosion evolution and stress corrosion cracking behavior of a low carbon bainite steel in the marine environments: Effect of the marine zones

Huiyun Tian,Zhongyu Cui,Heng Ma,Peilin Zhao,Maoxin Yan,Xin Wang,Hongzhi Cui

DOI: https://doi.org/10.1016/j.corsci.2022.110490

IF: 7.72

2022-09-01

Corrosion Science

Abstract:The effect of electrolyte presence form on the corrosion evolution and stress corrosion cracking (SCC) behavior of E690 steel in the simulated marine environment is investigated. The steel exhibits the highest and lowest corrosion rate in splash and immersion environment, respectively, attributed to the differences in oxygen availability, rust layer property, and scour stress. γ-FeOOH dominates the rust formed in atmospheric environment, while Fe3O4 prevails in the splash environment. The steel corroded in splash environment exhibits the high pit number density, high maximum pit depth, and high cathodic reaction activity, resulting in the most severe SCC degradation.

materials science, multidisciplinary,metallurgy & metallurgical engineering

Coupling Effect of Hydrostatic Pressure and Erosion on Corrosion Behavior of X70 Steel in Simulated Seawater

Effect of hydrostatic pressure on galvanic corrosion of low-alloy steel in simulated deep-sea environments

Effect of Rotating Speed and Hydrostatic Pressure on Erosion- Corrosion Behavior of X65 Pipeline Steel

Corrosion behavior of the low alloy weathering steels coupled with stainless steel in simulated open atmosphere

Hydrostatic pressure effects on corrosion behaviour of X80 steel in artificial sea water

Influence of Hydrostatic Pressure on the Pitting Corrosion Behavior of API X80 Steel

Effects of Environmental Factors on Corrosion Behavior of E690 Steel in Simulated Marine Environment

Synergistic effects of fluid flow and hydrostatic pressure on the degradation of epoxy coating in the simulated deep-sea environment

Effect of cathodic polarizations on the failure behavior of epoxy coating/low alloy steel systems under high hydrostatic pressure

A Statistical Study on the Effect of Hydrostatic Pressure on Metastable Pitting Corrosion of X70 Pipeline Steel

Effect of Hydrogen Charging on the Stress Corrosion Cracking Behavior of X70 Steel in Simulated Deep Seawater Environment

Impact of Multi-Factor Coupling on the Corrosion Behavior of 254smo Stainless Steel in an Aggressive Oilfield Environment Containing Co2 and H2s

Electrochemical corrosion behavior of high strength steel in simulated deep-sea environment under different hydrostatic pressure

Corrosion form transition of mooring chain steel in simulated deep-sea environments: remarkable roles of dissolved oxygen and hydrostatic pressure

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Tribocorrosion of 316L stainless steel by in-situ electrochemical methods under deep-sea high hydrostatic pressure environment

Erosion–corrosion behavior of X65 carbon steel in oilfield formation water

Synergistic effect between fluid flow and hydrostatic pressure on the failure behaviour of epoxy coating under deep ocean hydrodynamic environment

Coupling Effects of pH and Dissolved Oxygen on the Corrosion Behavior and Mechanism of X80 Steel in Acidic Soil Simulated Solution

Erosion–Corrosion Behavior of Friction Stud Welded Joints of X65 Pipelines in Simulated Seawater under Different Flow Rates

Corrosion evolution and stress corrosion cracking behavior of a low carbon bainite steel in the marine environments: Effect of the marine zones