Effects of the phase content and grain size on the electrical and energy storage properties of lead-free BNBT ceramics with substituted La3+

Bhoowadol Thatawong,Aurawan Rittidech,Naratip Vittayakorn,Theerachai Bongkarn

DOI: https://doi.org/10.1080/00150193.2022.2130781

2022-12-19

Ferroelectrics

Abstract:Lead-free [(Bi 0.5 Na 0.5 ) 0.94 Ba 0.06 ] 1-x La x TiO 3 (BNBT-xLa) ceramics with x = 0, 0.01, 0.02, 0.03, 0.04, 0.05 and 0.06 mol.% were synthesized by the solid-state combustion technique with calcination and sintering temperatures of 750 °C and 1150 °C, respectively, for 2 h. The phase formation, microstructure, dielectric, ferroelectric and energy storage properties of the BNBT-xLa ceramics were investigated. The XRD patterns of the powders showed a pure perovskite phase for all samples. The average particle size increased from 298 to 379 nm with increasing x. All ceramics showed coexisting rhombohedral and tetragonal phases. When x rose, the content of the tetragonal phase increased, as validated by the Rietveld refinement method. The average grain size decreased from 1.43 to 0.81 μm when x increased from 0 to 0.05 and then started to increase. The Curie temperature ( T d ) of the samples shifted to lower temperatures with rising x, owing to an increased tetragonal phase. The maximum dielectric constant ( ε m ), remanent polarization ( P r ) and coercive field ( E c ) decreased with increasing x. The BNBT-0.05La ceramic exhibited the smallest grain size, and lowest P r = 0.8 μ C/cm 2 and E c = 2.9 k V/cm, with the highest energy storage efficiency ( η ∼ 78.31%) and a large effective energy storage density ( W ∼ 0.83 J/cm 3 ) measured in an electric field of 80 kV/cm.

materials science, multidisciplinary,physics, condensed matter