Improving energy storage density, piezoelectric, and energy harvesting performances of eco-friendly (Bi0.49−xBaxLa0.01Na0.40K0.10)TiO3 ceramics by composition design strategy
Parkpoom Jarupoom,Pimpilai Wannasut,Orawan Khamman,Anucha Watcharapasorn,Pharatree Jaita
DOI: https://doi.org/10.1007/s10832-024-00377-7
2024-11-16
Journal of Electroceramics
Abstract:In this research, eco-friendly (Bi 0.49− x Ba x La 0.01 Na 0.40 K 0.10 )TiO 3 or BiBa x LNKT ceramics (where x = 0–0.15 mol fraction) were fabricated by solid-state mixed oxide technique, and their phase evolution, physical, microstructure, mechanical, dielectric, piezoelectric, ferroelectric, energy storage density, and energy harvesting properties have been systematically investigated. All ceramics exhibited a single perovskite structure. With increasing Ba content, a phase transition from mixed rhombohedral-tetragonal to be more tetragonal-rich phase was observed. The addition of Ba inhibited grain growth and resulted in densification, mechanical, and dielectric improvement. The maximum values of HV (6.01 GPa), HK (5.78 GPa), E (78 GPa), K IC (1.38 MPa.m 1/2 ), ε r (1604), and tan δ (0.0504) were observed for the x = 0.15 ceramic. The x = 0.15 ceramic also showed excellent piezoelectric performances ( d 33 = 248 pC/N, g 33 = 17.46 × 10 −3 Vm/N, and k p = 49%) and good off-resonance figure of merit (FoM) for energy harvesting (4.33 pm 2 /N). Moreover, after the introduction of Ba content, the ferroelectric long-range order is broken, which contributes to energy storage density improvement. Especially, the x = 0.05 ceramic achieved excellent recoverable energy storage density ( W rec = 1.31 J/cm 3 ) and good energy storage efficiency ( η = 96.18%) at 150 °C under driving electric fields ( E ) of 75 kV/cm. All results indicated that we can efficiently fabricate an environment-friendly (Bi 0.49− x Ba x La 0.01 Na 0.40 K 0.10 )TiO 3 system with good reliability for energy harvesting and high-temperature energy storage capacity applications.
materials science, ceramics