Abstract:Single crystals of lithium, sodium, and potassium titanates were grown with high-temperature constant-voltage electrolysis of TiO 2 with A 2 MoO 4 ( A = Li, Na, and K) as fluxes. Using the potassium-containing flux, needle-like crystals of hollandite-type K x Ti 8 O 16 with the maximum length of ~ 1 mm were successfully obtained. On the other hand, needle-like crystals of Na 2+ x Ti 6 O 13 and ramsdellite-type Li 2+ x Ti 3 O 7 with the maximum length of ~ 3 mm were grown when employing the sodium- and lithium-containing fluxes, respectively. This report demonstrates that the electrochemical crystal growth is favorable to obtain titanates with various one-dimensional tunnel structures upon varying the alkali-metal elements. A diversity in structural types of the resultant single crystals is reasonably explained in terms of the ionic size of alkali metals incorporated.

Structural Design of Alkali-Metal Titanates: Electrochemical Growth of KxTi8O16, Na2+xTi6O13, and Li2+xTi3O7 Single Crystals with One-Dimensional Tunnel Structures