Abstract:In this study, polyurethane (PU) foams were manufactured using kraft lignin and castor oil as bio-based polyols by replacing 5–20 wt% and 10–100 wt% of conventional polyol, respectively. To investigate the effects of unmodified bio-based polyols on PU foam production, reactivity and morphology within PU composites was analyzed as well as mechanical and thermal properties of the resulting foams. Bio-based PU foam production was carried out after characterizing the reagents used in the foaming process (including hydroxyl group content, molecular weight distribution, and viscosity). To compare the resulting bio-based PU foams, control foam were produced without any bio-based polyol under the same experimental conditions. For lignin-incorporated PU foams, two types, LPU and lpu, were manufactured with index ratio of 1.01 and 1.3, respectively. The compressive strength of LPU foams increased with lignin content from 5 wt% (LPU5: 147 kPa) to 20 wt% (LPU20: 207 kPa), although it remained lower than that of the control foam (PU0: 326 kPa). Similarly, the compressive strength of lpu foams was lower than that of the control foam (pu0: 441 kPa), with values of 164 kPa (lpu5), 163 kPa (lpu10), 167 kPa (lpu15), and 147 kPa (lpu20). At 10 wt% lignin content, both foams (LPU10 and lpu10) exhibited the smallest and most homogenous pore sizes and structures. For castor oil-incorporated PU foams with an index of 1.01, denoted as CPU, increasing castor oil content resulted in larger cell sizes and void fractions, transitioning to an open-cell structure and decreasing the compressive strength of the foams from 284 kPa (CPU10) to 23 kPa (CPU100). Fourier transform infrared (FT-IR) results indicated the formation of characteristic urethane linkages in PU foams and confirmed that bio-based polyols were less reactive with isocyanate compared to traditional polyol. Thermogravimetric analysis (TGA) showed that incorporating lignin and castor oil affected the thermal decomposition behavior. The thermal stability of lignin-incorporated PU foams improved as the lignin content increased with char yields increasing from 11.5 wt% (LPU5) to 15.8 wt% (LPU20) and from 12.4 wt% (lpu5) to 17.5 wt% (lpu20). Conversely, the addition of castor oil resulted in decreased thermal stability, with char yields decreasing from 10.6 wt% (CPU10) to 4.2 wt% (CPU100). This research provides a comprehensive understanding of PU foams incorporating unmodified biomass-derived polyols (lignin and castor oil), suggesting their potential for value-added utilization as bio-based products.

Hydroxymethylation of technical lignins obtained from different pretreatments for preparation of high-performance rigid polyurethane foam

Modification of Renewable Resources-Lignin-by Three Chemical Methods and Its Applications to Polyurethane Foams

Preparation of rigid polyurethane foam from lignopolyol obtained through mild oxypropylation

High-value utilization of hydroxymethylated lignin in polyurethane adhesives.

Preparation of Mechanically Robust Bio-Based Polyurethane Foams Using Depolymerized Native Lignin

Successive organic solvent fractionation and homogenization of technical lignin for polyurethane foam with high mechanical performance

Signally improvement of polyurethane adhesive with hydroxy-enriched lignin from bagasse

Kraft lignin-containing polyurethane adhesives: the role of hydroxypropylation on thermomechanical properties

Fractionated lignin as a polyol in polyurethane fabrication

Lignins as macromonomers for polyurethane synthesis: A comparative study on hydroxyl group determination

Bio-based polyurethane foam preparation employing lignin from corn stalk enzymatic hydrolysis residues

Study on Preparation and Properties of Cellulose Ethanol Lignin Based Polyurethane Foam

Highly Resilient Lignin-Containing Polyurethane Foam

Preparation of bio-polyols by liquefaction of hardwood residue and their application in the modification of polyurethane foams

Preparation of a Polyhydric Aminated Lignin and Its Use in the Preparation of Polyurethane Film

Functionalized Lignin for Halogen-Free Flame Retardant Rigid Polyurethane Foam: Preparation, Thermal Stability, Fire Performance and Mechanical Properties

Investigation of bio-based rigid polyurethane foams synthesized with lignin and castor oil

Study on utilization of acetic acid lignin in synthesis of polyurethane foams

Preparation and Performance Characterization of Alkali Lignin-based Rigid Polyurethane Foam

Performance characterization of rigid polyurethane foam with refined alkali lignin and modified alkali lignin

Lignin Polyurethane Aerogels: Influence of Solvent on Textural Properties