Carbonation-hardening properties and ITZ microstructure of low-calcium CO2 sequestration binder mortar
Xiangxiang Chang,Songhui Liu,Cheng Zhang,Peiliang Shen,Dongxing Xuan,Xuemao Guan,Caijun Shi
DOI: https://doi.org/10.1016/j.conbuildmat.2022.127589
IF: 7.4
2022-06-01
Construction and Building Materials
Abstract:To produce high-strength prefabricated building materials and reduce their CO2 emissions, a new low calcium CO2 sequestration binder (LC-CSB) was prepared by calcination of industrial raw materials limestone and sandstone at 1275 °C. The physical and mechanical properties development of the LC-CSB mortar was investigated at different carbonation durations (5 min, 10 min, 30 min, 1 h, 8 h, 24 h). Moreover, the microstructure and micromechanical properties of the interfacial transition zone (ITZ) between carbonated LC-CSB paste and siliceous river sand aggregate were revealed by SEM and nanoindentation. The results showed that the compressive strength of the LC-CSB mortar reached 43.2 MPa after carbonation for 24 h. The ITZ was more easily carbonated than the LC-CSB paste, and the calcite crystals generated after carbonation will be enriched at the ITZ with the increase of carbonation duration, while the porosity was significantly reduced.
construction & building technology,materials science, multidisciplinary,engineering, civil