Abstract:The induced impacts of high doses of gamma irradiation on the structural variations of poly-allyl-diglycol carbonate (PADC) polymers (CR-39) were studied in terms of X-ray diffraction (XRD) patterns. CR-39 samples were irradiated separately at different ranging from 200 to 800 kGy; (step 200). A deconvolution process of the XRD spectra of CR-39 samples for all gamma irradiation doses was performed. The results of this deconvolution process for the pristine specimen show three diffraction peaks at about 20.30°, 28.16° and 41.70° of 2 θ . The broad peaks at 28.16 o and 41.70°, and the highest peak at 20.30° of XRD confirm the amorphous nature and low degrees of crystallinity, respectively. The position, area, intensity and full width at half maximum of these peaks are changed with further doses of gamma irradiation. With additional gamma irradiations, the intensities of all peaks decrease significantly. The highest and sharpest peak properties are employed to determine the crystallinity, crystallite size, and radiation chemical yield (G-value) for the loss of carbonate ester bonds using a proposed method. Higher doses of gamma irradiation result in a decrease in crystallinity while increasing crystallite size. Furthermore, the optical band gaps reduced from 4.81 to 3.49 eV when the irradiated dose increased from 0 to 800 kGy. Furthermore, the third order nonlinear susceptibility increased from 0.84x10 −12 esu to 2.25x10 −12 esu with increasing the radiation doses from 0 to 800 kGy. Moreover, the nonlinear refractive increased from 1.52x10 −11 to 3.69x10 −11 with increasing the radiation doses from 0 to 800 kGy. On the other hand, the number of carbon atoms in each cluster increased from 51 to 97 when the irradiated dose increased from 0 kGy to 800 kGy.

UV effect on etching parameters and activation energy of CR-39 plastic detector

Effects of Storage Time and Pre-Etching Treatment of CR-39 Detectors on Their Response to Alpha Radiation Exposure

UVC irradiation of alpha particles tracks and empirical equation of bulk etch rate in CR-39 detector

Estimation of alpha exposure on CR-39 detector using a UV-VIS spectrophotometer

Studies of chemical bonds loss and optical modifications of CR-39 caused by gamma rays

Direct and indirect determination of track etch parameters after sequential UV-C exposure and etching for two swift heavy ions in PADC: Production of rocket-shaped tracks

Spectroscopic and electrical changes in Lr-115 type II nuclear track detector before and after gamma radiation

Surface Effect of Ultraviolet Radiation on Electrochemically Etched Alpha-Particle Tracks in PADC

Attenuation of electromagnetic radiation in Nuclear Track Detectors

Irradiation effect of new scintillators

Energy Calibration of a CR-39 Nuclear-Track Detector Irradiated by Charged Particles

A comparative study of alternative methods to determine the response of poly-ethylene terephthalate nuclear track detector

Experimental Study on CR-39 Response to Alpha Particles with Different Incident Angles and Energy

Chemical damage around Xe ion tracks in Poly(allyl diglycol carbonate) PADC track detector

Dose rate effects in radiation-induced changes to phenyl-based polymeric scintillators

A study of radiation damage and heat annealing effect on the irradiated 3T active pixel sensor

Effects of neutron radiation on the optical and structural properties of blue and green emitting plastic scintillators

An Improved Electrostatic Integrating Radon Monitor with the CR-39 As Alpha-Particle Detector.

Study on radiation damage effects on CdZnTe detectors under 3 MeV and 2.08 GeV Kr ion irradiation

Post-radiation phenomena in thermally treated Kr matrices

Comparison of Morphological Characteristics for Alpha Tracks in CR-39 Using Different Radon Monitors