Synergetic effects of the co-doping transition metal ions and the silica-shell coating for enhancing the photoluminescence and stability of Mn: CsPbCl 3 nanocrystals and their application
Rui Zhang,Gang Chen,Haiyun Liu,Jianfeng Zhang,Yaoxin Yuan,Zehua Lv,Lifu Zhang,Chunlan Wang,Zhenxing Qin,Wen Yang,Jinbin Wang
DOI: https://doi.org/10.1016/j.optmat.2022.113308
IF: 3.754
2022-12-16
Optical Materials
Abstract:Doping Mn 2+ ions into cesium lead halide CsPbX 3 (X = Cl, Br, I) perovskite nanocrystals (PNCs) has been proven to be an effective strategy to reduce the Pb 2+ content. However, excessive Mn 2+ ions may form the Mn–Mn dimers in PNCs, leading to concentration quenching effects and low photoluminescence quantum yields (PLQYs). Herein, secondary metal ions (Ni 2+ , Cu 2+ , Zn 2+ ) were introduced to substitute Pb 2+ ions as co-doped (Mn, M):CsPbCl 3 PNCs (M = Ni, Cu, Zn), which were prepared by a facile method under ambient conditions, aiming for positively passivating the surface defects and improving the Mn 2+ emission. Also, to protect the co-doped (Mn, M):CsPbCl 3 PNCs from moisture damage, we performed silica encapsulation, which further passivated surface defects due to the effective hydrolysis of silane. The evolution of optical properties and stabilities of three series of (Mn, M):CsPbCl 3 PNCs was compared. The PLQYs of co-doped (Mn, M):CsPbCl 3 PNCs were larger than those of single-doped Mn: CsPbCl 3 PNCs, especially for (Mn, Ni):CsPbCl 3 and (Mn, Cu):CsPbCl 3 , which can reach nearly 30%. The PLQYs of (Mn, Ni):CsPbCl 3 and (Mn, Zn):CsPbCl 3 PNCs decreased dramatically during the encapsulation process, while the PLQY values of (Mn, Cu):CsPbCl 3 remained 30% even after the same treatment process. Consequently, the prototypes of white light-emitting devices (WLEDs) were successfully fabricated based on orange-red (Mn, Ni):CsPbCl 3 @SiO 2 and (Mn, Zn):CsPbCl 3 @SiO 2 composites. The synergetic effects of co-doping transition metal ions and silica-shell coating on improving optical properties and stabilities were investigated. It has potential for a wide range of applications in the field of solid-state light emission.
materials science, multidisciplinary,optics