Abstract:The use of carbon fiber reinforced plastic (CFRP) is rapidly increasing in aerospace and automobile applications. This is in large part due to the increase strength and modulus of carbon fiber composites compared to other materials such as glass fiber composites. The fiber-matrix interface has been found to be important for high strength in composites. Methods that have been studied and developed to improve interfacial property of composites include: the addition of coupling agents, surface modifications, chemical reaction control and use of nano-fillers for reinforcement. During mechanical loading the shape of carbon fibers, in a composite, is altered with a concomitant change in electrical resistance. Carbon fibers are used as sensing elements in CFRP due to their electrical conductivity. In some more advanced studies, in CRFP, the carbon fibers were used for both strain sensing and damage sensing. The basic theory, in such studies, was that the movement of carbon fiber could be detected by electrical resistance measurement. During loading, the extent of contact between carbon fibers in a CF tow is altered, and the electrical resistance changes from its initial value. In this work, interfacial properties of carbon fiber/polymer composites were evaluated by such electrical resistance measurements. During the wetting process of CF tows by the polymer resins, the change in electrical resistance was recorded and analyzed. The test results for different carbon fibers and polymer resins exhibited different trends. The electrical resistance change was associated with the different wetting conditions, and the interfacial properties were predicted by these electrical resistance measurements. CF tow/epoxy exhibited the poorest carbon tow wettability, the smallest change in resistance and the poorest IFSS and ILSS. For the four systems studied, the relative change in each of these quantities for the materials of a given composite was roughly proportional to the other measured quantities. This may have some very significant practical importance. It may point the way to use quick easy tests to screen and predict other behaviors for composites of different materials and/or processes. Perhaps a simple resistance change test might be used to predict and select good candidate materials, surface processing techniques for high strength composite applications. The proportional relationship between interfacial adhesion and electrical resistance change was obtained by trend fitting line analyses. Ultimately, it was demonstrated that mechanical properties related to interfacial properties might potentially be predicted by electrical resistance measurement and studies of wetting behavior, using empirical formulas and correlations.

Influence of the Surface Film (Third Body) on the Friction and Wear Process of Carbon-Fiber Composites

Effect of wear particles and roughness on nanoscale friction

Friction and Wear Behaviors of Surface-Modified Carbon Fabric/Epoxy Resin Composites

Influence of material and orientation of carbon fibers on tribological properties of fabric composites

Tribological Properties of a Carbon Fabric Composite with Different Orientations of Fabric Layers to the Movement Direction during Friction

Influence of Running-In on the Friction Coefficient of C/C Composite Materials for Aircraft Brakes

Surface topography modification, Film transfer and Wear mechanism for fibre reinforced polymer composites—An Overview

Friction and Wear Properties of Carbon/carbon Composites with Different Martix Carbon

Friction and Wear Performance of Staple Carbon Fabric-Reinforced Composites: Effects of Surface Topography

Interfacial Evaluation Of Carbon Frinforced Nano-Composites Using Electrical Resistance Measurement With Wetting Tests

Testing and Analysis of Frictional Performance of Carbon Fiber/Metal Composite Materials

Determination of Wear, Friction Behavior and Characterization of Carbon Fiber Reinforced Epoxy Composites for Transport Applications

Dry Friction and Wear Behavior of Laser-Sintered Graphite/Carbon Fiber/Polyamide 12 Composite

Contact size effects on the friction and wear of amorphous carbon films

DRY SLIDING FRICTION and WEAR PROPERTIES of CACO3 NANOPARTICLE FILLED EPOXY/CARBON FIBER COMPOSITES

The effect of third bodies on wear and friction at the wheel-rail interface

Influence of Composition on Friction-Wear Behavior of Composite Materials Reinforced by Brass Fibers

Friction and Wear Properties of Pitch/resin Densified Carbon Carbon Composites Used for Airbrakes

Effect of CaF2 surface layers on the friction behavior of copper-based composite

Influence of MoS2 nano-filler additions on wear behavior of carbon fiber reinforced epoxy composites

Wear and environmental aspects of composite materials for automotive braking industry