Facile surface coating of Ni–Co–P alloy particles on hollow glass microspheres for enhanced wave absorbing

Haimeng Huang,Pengcheng Song,Fan Bu,Lei Liu,Yahui Liu,Chuanhua Xu,Jianfeng Zhang

DOI: https://doi.org/10.1007/s10854-022-08579-x

2022-06-22

Abstract:The surface coating of magnetic nanoparticles onto hollow glass microspheres (HGMs) is of vital importance as light-weighted powders with wave-absorbing properties. In this study, HGMs were successfully coated by Co/Ni nanoparticles through a four-stepped strategy of NaF + HCl roughening, NaOH washing, PdCl 2 activation, and electroless plating, successively. The soft roughening of SiO 2 with NaF and the post-washing of Na 2 SF 6 byproducts with NaOH were validated to ensure the integrity of the as-coated HGMs. The Ni–Co–P alloy coatings were measured to be lower than 1 μm in thickness with nanoparticles of 100–200 nm in diameter. The reflection loss of HGMs coated by 30 wt% Ni/Co not only retained the peak of the Co coating (− 4.5 dB) but also reached about − 6.7 dB at 16.4 GHz, much higher than that of HGMs coated by Ni and Co. The overall trend of input and output impedance ratio of the sample coated by Ni/Co does not change significantly compared with HGMs coated by Co, but the impedance matching has been optimized compared with Ni-plated powders. The novel light material with a uniform and complete coating prepared in this paper provides a new idea for the modification of HGMs for multi-functional applications.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied