Enhance Luminescence or change morphology: The effect of doping method on Cu2+-doped CsPbBr3 perovskite nanocrystals

Meng Li,Yang Song,FeiYong Chen

DOI: https://doi.org/10.1039/d2ce01302a

IF: 3.756

2022-10-19

CrystEngComm

Abstract:Although various cations were explored as the substitute for Pb2+ in CsPbX3 nanocrystals (NCs), there was few research to study the influence of doping methods on doping results. Cu2+ as the transition metal with low toxicity, there were limited studies of Cu2+-doped CsPbX3 NCs, especially in the effect of doping methods. Herein, Cu2+ was successful doped into CsPbBr3 NCs with the replacement of Pb2+ via hot injection method and postsynthetic cation exchange reaction. Using hot-injection method, introducing of additional Cu2+ promoted the formation of CsPbBr3 nanoplates with uniformly thickness. The size of CsPbBr3 nanoplates increased with increasing the temperature. Differently, using postsynthetic cation exchange reaction, doping moderate Cu2+ ion into CsPbBr3 NCs obviously improved the PLQY, prolonged the PL lifetime, and decreased the non-radiative decay, resulting from the effective passivation of surface defects on CsPbBr3 NCs. The different effect of Cu2+ was the outcome of how the CuBr2 interacted with the CsPbBr3 NCs in different protocols. Our results promoted the further research on the substitute Pb2+ with other cations, provided the effective protocols to prepare low dimensional CsPbBr3 nanoplates with uniformly thickness and easily controlled lateral size, and achieved the enhancement of PLQY of CsPbBr3 NCs, which will be benefit to the further development of CsPbX3 in optoelectronic and other fields.

chemistry, multidisciplinary,crystallography