Abstract:Multi-pass TIG welding was conducted on plates (15×300×180 mm<sup>3</sup>) of aluminum alloy Al-5083 that usually serves as the component material in structural applications such as cryogenics and chemical processing industries. Porosity formation and solidification cracking are the most common defects when TIG welding Al-5083 alloy, which is sensitive to the welding heat input. In the experiment, the heat input was varied from 0.89 kJ/mm to 5 kJ/mm designed by the combination of welding torch travel speed and welding current. Tensile, micro-Vicker hardness and Charpy impact tests were executed to witness the impetus response of heat input on the mechanical properties of the joints. Radiographic inspection was performed to assess the joint's quality and welding defects. The results show that all the specimens displayed inferior mechanical properties as compared to the base alloy. It was established that porosity was progressively abridged by the increase of heat input. The results also clinched that the use of medium heat input (1 to 2 kJ/mm) offered the best mechanical properties by eradicating welding defects, in which only about 18.26 % of strength was lost. The yield strength of all the welded specimens remained unaffected indicated no influence of heat input. Partially melted zone (PMZ) width also affected by heat input, which became widened with the increase of heat input. The grain size of PMZ was found to be coarser than the respective grain size in the fusion zone. Charpy impact testing revealed that the absorbed energy by low heat input specimen (welded at high speed) was greater than that of high heat input (welded at low speed) because of low porosity and the formation of equiaxed grains which induce better impact toughness. Cryogenic (-196 °C) impact testing was also performed and the results corroborate that impact properties under the cryogenic environment revealed no appreciable change after welding at designated heat input. Finally, Macro and micro fractured surfaces of tensile and impact specimens were analyzed using Stereo and Scanning Electron Microscopy (SEM), which have supported the experimental findings.

Effect of Tungsten Inert Gas Welding Parameters on Hot Crack Sensitivity of Cast Magnesium Alloy

Hot Cracking of Resistance Spot Welded Magnesium Alloy

Effect of ultrasonic amplitude on GTAW crack sensitivity of AZ91D

Effect of heat input of TIG repair welding on microstructure and mechanical properties of cast AZ91 magnesium alloy

Effect of Welding Current on Microstructure and Properties of TIG Welded EW75 Magnesium Alloy

Effects of Component of Weld Wire on Susceptibili ty of Hot Weld Crack of LC9CS Aluminum Alloy

Microstructures and Mechanical Properties of Resistance Spot Welded Magnesium Alloy Joints

Effect of Welding Defects on Mechanical Properties of Welded Joints Subjected to Temperature

Effect of Welding Current and Speed on Solidification Cracking Susceptibility in Gas Tungsten Arc Fillet Welding of Dissimilar Aluminum Alloys: Coupling a Weld Simulation and a Cracking Criterion

Effect of shielding gas composition and welding speed on autogenous welds of unalloyed tungsten plates

Influence of TIG welding process parameters on microstructure and mechanical properties of as-cast Mg-8Li-3Al-2Zn-0.5Y alloy

Research on TIG repairing technology for ZM6 magnesium alloy casting

Effect of Cold Metal Transfer Welding Repair Parameters on the Forming for the Repair of Surface Defects of Cast Magnesium Alloy

Investigation of cracks during electron beam welding of γ-TiAl based alloy

Effect of Ti on Hot Cracking and Mechanical Performance in the Gas Tungsten Arc Welds of Copper Thick Plates

The Effect of TIG Welding Parameters and Automatization for Non-Heat Treated Inconel 718 Sheets

Controlling hot cracking in Ni-based Inconel-718 superalloy cast sheets during tungsten inert gas welding

A Comprehensive Analysis of Ultrasonic Pulse Current Reducing Hot Cracking in Inconel 718 Welds

Effect of welding parameters on microstructure, mechanical properties and environment

Investigation on the process parameters of TIG-welded aluminum alloy through mechanical and microstructural characterization

Prediction of the influence of welding metal composition on solidification cracking of laser welded aluminum alloy