Abstract:Platinum-based catalysts are widely used for efficient catalysis of the acidic oxygen reduction reaction (ORR). However, the agglomeration and leaching of metallic Pt nanoparticles limit the catalytic activity and durability of the catalysts and restrict their large-scale commercialization. Therefore, this study aimed to achieve a uniform distribution and strong anchoring of Pt nanoparticles on a carbon support and improve the ORR activity and durability of proton-exchange membrane fuel cells. Herein, we report on the facile one-pot synthesis of a novel ORR catalyst using metal–nitrogen–carbon (M–N–C) bonding, which is formed in situ during the ion exchange and pyrolysis processes. An ion-exchange resin was used as the carbon source containing R-N+(CH3)3 groups, which coordinate with PtCl62− to form nanosized Pt clusters confined within the macroporous framework. After pyrolysis, strong M-N-C bonds were formed, thereby preventing the leaching and aggregation of Pt nanoparticles. The as-synthesized Pt supported on the N-doped hierarchically porous carbon catalyst (Pt/NHPC-800) showed high specific activity (0.3 mA cm−2) and mass activity (0.165 A mgPt−1), which are approximately 2.7 and 1.5 times higher than those of commercial Pt/C, respectively. The electrochemical surface area of Pt/NHPC-800 remained unchanged (~1% loss) after an accelerated durability test of 10,000 cycles. The mass activity loss after ADT of Pt/NHPC-800 was 18%, which is considerably lower than that of commercial Pt/C (43%). Thus, a novel ORR catalyst with highly accessible and homogeneously dispersed Pt-N-C sites, high activity, and durability was successfully prepared via one-pot synthesis. This facile and scalable synthesis strategy for high-efficiency catalysts guides the further synthesis of commercially available ORR catalysts.

Kirkendall effect-driven formation of hollow PtNi alloy nanostructures with enhanced oxygen reduction reaction performance

Engineering Porosity into Trimetallic PtPdNi Nanospheres for Enhanced Electrocatalytic Oxygen Reduction Activity

Hollow PtCo alloy nanostructures for efficient oxygen reduction electrocatalysis in polymer electrolyte membrane fuel cells

Multimetallic AuPd@Pd@Pt Core-Interlayer-shell Icosahedral Electrocatalysts for Highly Efficient Oxygen Reduction Reaction

Engineering Platinum–nickel Nano-Alloys in Hierarchically Ordered Porous Cobalt-Nitrogen-doped Carbon for Highly Efficient Electrocatalytic Oxygen Reduction

High‐Temperature Confinement Synthesis of Supported Pt–Ni Nanoparticles for Efficiently Catalyzing Oxygen Reduction Reaction

Nanoporous Surface Alloys As Highly Active and Durable Oxygen Reduction Reaction Electrocatalysts

PtNi Alloy Nanoparticles Grown in situ on Nitrogen doped Carbon for Efficient Oxygen Reduction Reaction

Octahedral Pd@Pt1.8Ni Core-Shell Nanocrystals with Ultrathin PtNi Alloy Shells As Active Catalysts for Oxygen Reduction Reaction.

Synthesis of Platinum Nanocrystals Dispersed on Nitrogen-Doped Hierarchically Porous Carbon with Enhanced Oxygen Reduction Reaction Activity and Durability

Zn-Introduced Platinum-Cobalt Intermetallic Catalyst for Oxygen Reduction Reaction

Highly Ordered Pt-Based Nanoparticles Directed by the Self-Assembly of Block Copolymers for the Oxygen Reduction Reaction

In Situ Alloying with Hybrid Mesoporous Fe-N-C to Accelerate the Catalysis Efficiency of Pt for the Oxygen Reduction Reaction

Pt–Ni Alloy Nanoparticles via High-Temperature Shock as Efficient Electrocatalysts in the Oxygen Reduction Reaction

Engineering Pt Nanoparticles with Fe and N Codoped Carbon to Boost Oxygen Reduction Catalytic Performance in Acidic Electrolyte

Ni–Pd core–shell nanoparticles with Pt-like oxygen reduction electrocatalytic performance in both acidic and alkaline electrolytes

Collaborative Anchoring of Pt Nanoparticles and Metal Oxide Nanoparticles on N-Doped Carbon as Catalysts for Oxygen Reduction

3D Porous Fe/N/C Spherical Nanostructures As High-Performance Electrocatalysts for Oxygen Reduction in Both Alkaline and Acidic Media.

N-doped Carbon-Stabilized PtCo Nanoparticles Derived from Pt@ZIF-67： Highly Active and Durable Catalysts for Oxygen Reduction Reaction

A Chemical Dealloying Approach for Pt Surface-enriched Pt 3 Co Alloy Nanoparticles as Oxygen Reduction Reaction Electrocatalysts

High Activity and Durability of Carbon-Supported Core-Shell PtPx@Pt/C Catalyst for Oxygen Reduction Reaction