Abstract:By comparing the advantages and disadvantages of the existing single‐step pressurized metallurgical manufacturing technologies of high nitrogen stainless steel (HNS), a promising pressurized duplex manufacturing route, i.e. pressurized induction melting (PIM) and pressurized electroslag remelting (PESR), was proposed. The PIM stage mainly carried on the nitrogen alloying, deoxidation and desulphurization, and PESR process mainly took responsibility for further desulphurization, removal of large‐size inclusion and elevating solidification quality. During PIM, the deoxidation was achieved by vacuum carbon deoxidation combined with magnesium and rare earth compound treatment. Subsequently, the PESR was conducted under high nitrogen pressure without adding nitrided ferroalloys. To precisely control the nitrogen content and avoid segregation and escape of nitrogen, the three‐stage nitrogen pressure collocation was developed. The high nitrogen stainless bearing steel 30Cr15Mo1N (DIN 1.4108) was manufactured as an example by the duplex route, and an PIM‐PESR ingot with high nitrogen content, high cleanliness, fine and dispersive inclusions, and compact solidification structure was obtained. Moreover, the steel possessed homogeneous microstructure, slightly better mechanical properties and corrosion resistance compared with that manufactured by the single‐step PESR process. Finally, a pressurized ladle refining and pressurized electroslag remelting duplex route was proposed for the purpose of large‐scale industrial production of HNSs. This article is protected by copyright. All rights reserved.

A promising pressurized duplex manufacturing route of high nitrogen stainless steel