Effect of σ Phase Precipitation on the Corrosion Resistance of Fe-Cr-Mn-Al Duplex Stainless Steel
Mingming Pan,Jun Zhang,Xiaoming Zhang
DOI: https://doi.org/10.1007/s11665-024-10258-3
IF: 2.3
2024-11-07
Journal of Materials Engineering and Performance
Abstract:In this study, a new type of duplex stainless steel was successfully developed through innovative composition design and special preparation process. Based on the composition of Fe-19Cr-1Ni-0.6Al-12Mn, the material uses Mn to replace part of Ni and Al to replace part of Cr, thus realizing cost optimization and performance improvement. The special feature is that ferrite phase becomes dominant during hot rolling, which significantly improves the corrosion resistance and mechanical properties of the material. In order to accurately control the austenite phase, cold rolling and annealing techniques were combined in the study. This kind of duplex stainless steel has excellent thermos-plasticity, mechanical properties and corrosion resistance, and the cost advantage is obvious. However, its corrosion resistance, especially σ phase precipitation behavior, still needs to be further studied, which is an important application challenge of duplex stainless steel. The experimental results show that the corrosion resistance of the experimental steel decreases greatly under low-temperature heat treatment, which is attributed to the precipitation of σ phase (chromium-rich) at the grain boundary during annealing at 780 °C, leading to the redistribution of alloy elements and chromium-poor phenomenon. The amount of σ phase precipitation changes with the increase in aging time, but compared with the traditional duplex stainless steel, the newly developed duplex stainless steel precipitates σ phase slowly. The reason behind this is that during the annealing process, the recovery recrystallization of ferrite in the structure is inhibited, which provides more time windows for the precipitation of σ phase. It can be seen that by optimizing the preparation process, we can effectively slow down the precipitation trend of σ phase and lay a foundation for improving the properties and application prospects of duplex stainless steel.
materials science, multidisciplinary