Effect of the grain size on the corrosion behavior of CoCrFeMnNi HEAs in a 0.5 M H2SO4 solution

Ying Wang,Junsong Jin,Mao Zhang,Xinyun Wang,Pan Gong,Jiacheng Zhang,Jianchun Liu

DOI: https://doi.org/10.1016/j.jallcom.2020.157712

IF: 6.2

2021-03-01

Journal of Alloys and Compounds

Abstract:This work investigated the corrosion behavior of the equiatomic CoCrFeMnNi high entropy alloy (HEA) in a 0.5 M H2SO4 solution. The grain size of the HEA was adjusted by annealing. The electrochemical analysis showed that the corrosion resistance of the CoCrFeMnNi HEA increases first and then decreases with the increase of grain size. When the grain size is lower than a certain value, increasing the grain size can improve the corrosion resistance. Fine-grained (≤1.24 μm) HEA forms abundant grain boundaries, which promotes the occurrence of galvanic corrosion at the grain boundaries with inter-grains, resulting in reduced corrosion resistance. However, coarse-grained (≥145.9 μm) HEA provides too few ionic diffusion channels to form a stable and continuous passive film, which also reduces the corrosion resistance. Nanoindentation and XPS tests showed that a high content of Fe (Ⅲ) oxides and Cr (Ⅲ) oxides are formed on the medium-grained HEA, which improves the chemical stability and mechanical strength of the passive films. Thus, the corrosion resistance of medium-grained HEA is much better than those of fine-grained and coarse-grained HEA.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the effect of grain size on the corrosion behavior of CoCrFeMnNi high - entropy alloy (HEA) in 0.5 M H₂SO₄ solution. Specifically, by adjusting the grain size, the author explored the variation law of the corrosion resistance of CoCrFeMnNi HEA with different grain sizes in an acidic environment and the underlying mechanism.

### Background and Problem of the Paper
High - entropy alloys (HEAs) show great potential in modern industrial applications due to their excellent high - temperature oxidation resistance, strong corrosion resistance, high hardness, high strength, and excellent wear resistance. However, corrosion can lead to the degradation of material properties, increasing service risks and waste. Therefore, the corrosion performance of new materials needs to be carefully evaluated. Previous studies have shown that the corrosion resistance of HEA can be improved by adjusting its composition, for example, by reducing the Al content or Mo content to expand the passive region and reduce the passive current density. In addition, changing the microstructure of HEA can also significantly affect its corrosion behavior.

### Research Objectives
This paper aims to systematically study the effect of grain size on the corrosion behavior of CoCrFeMnNi HEA in 0.5 M H₂SO₄ solution. Specific objectives include:
1. **Adjustment of Grain Size**: Adjust the grain size of CoCrFeMnNi HEA through annealing treatment.
2. **Electrochemical Analysis**: Use potentiodynamic polarization tests and electrochemical impedance spectroscopy (EIS) measurements to analyze the electrochemical corrosion mechanism and passivation behavior of HEA at different grain sizes.
3. **Mechanical Properties and Surface Morphology Analysis**: Through nano - indentation tests and X - ray photoelectron spectroscopy (XPS) analysis, study the mechanical properties and chemical composition of the passivation film.

### Main Findings
- **Fine - grained HEA (≤ 1.24 µm)**: Abundant grain boundaries are formed, which promotes galvanic corrosion between the grain boundaries and the grains, resulting in a decrease in corrosion resistance.
- **Medium - grained HEA (about 71.6 µm)**: A high content of Fe oxides and Cr oxides is formed, which improves the chemical stability and mechanical strength of the passivation film, thereby significantly increasing the corrosion resistance.
- **Coarse - grained HEA (≥ 145.9 µm)**: Too few ion diffusion channels are provided, making it difficult to form a stable and continuous passivation film, resulting in a decrease in corrosion resistance.

### Conclusions
The study shows that the corrosion resistance of CoCrFeMnNi HEA first increases and then decreases as the grain size increases. The HEA with a medium grain size has the best corrosion resistance, which is mainly attributed to the higher chemical stability and mechanical strength of the passivation film formed.

### Formula Display
The formulas involved in the paper are as follows:

1. **Impedance Definition of CPE (Constant Phase Angle Element)**:
\[
Z_{\text{CPE}}=\left[Y_0(j\omega)^n\right]^{-1}
\]
where \(Y_0\) is the proportionality factor, \(j\) is the imaginary unit, \(\omega = 2\pi f\), and \(n\) is the phase shift, ranging from 0 to 1.

2. **Calculation of Double - layer Capacitance \(C_{\text{dl}}\)**:
\[
C_{\text{dl}}=\frac{Y_0}{(R_{\text{s}}+R_{\text{p}})(j\omega)^n}
\]

3. **Mott - Schottky Equation**:
\[
\frac{1}{C^2}=\frac{2}{\epsilon\epsilon_0}(N_d - N_a)\left(E - E_{\text{fb}}-\frac{kT}{q}\ln\left(\frac{N_d - N_a}{N_i}\right)\right)
\]
where \(\epsilon\) is the dielectric constant of the passivation film, \(\epsilon_0\) is the vacuum dielectric constant, \(N_d\) is the donor density, \(N_a\) is the acceptor density, \(E_{\text{fb}}\)