Impact of Partitioning Temperature Parameters during the Quenching and Partitioning Process on Medium Carbon Steels with Two Different Alloying Strategies
Mattia Franceschi,Giulia Stornelli,Roberto Perrone,Luca Pezzato,Andrea Di Schino,Manuele Dabalà
DOI: https://doi.org/10.1002/srin.202400710
IF: 2.1258
2024-11-18
steel research international
Abstract:The study investigates microstructural evolution during high‐temperature partitioning in medium‐carbon, high‐silicon aluminum‐aided steels, exploring phase transformations affecting the final microstructure. Quenching and partitioning processes, with varying primary martensite fractions, reveal significant austenite stabilization at 350 °C, but deviations from constrained carbon equilibrium occurred. At 450–550 °C, tempering reactions like cementite precipitation and pearlite formation reduce the retained austenite fraction over time. Quenching and partitioning (Q&P) heat treatments have recently gained attention as promising methods for the third generation of advanced high‐strength steels, particularly in industrial applications like automotive. This study investigates the microstructural evolution during Q&P in two medium‐carbon high‐silicon and aluminum‐alloyed steels, exploring potential additional phase transformations controlling the final structure. The choice to focus on Si and Al‐ medium‐carbon steel is linked to the lower cost of these elements compared to commonly alloying elements like Ti, Cr, Mo, and V, while still achieving high mechanical properties through Q&P. The Q&P process is analyzed by varying the volume fraction of primary martensite (M1) at 0.25, 0.50, and 0.75, with partitioning temperatures ranging from 350 to 550 °C for 30 min. At 350 °C, a significant volume fraction of stabilized austenite (up to 0.3) is observed. However, concurrent reactions such as nanostructured bainite and martensite formation lead to deviations from the theoretical constrained carbon equilibrium (CCE). At higher temperatures (450–550 °C), tempering reactions, including cementite precipitation and pearlite formation, reduced the austenite final fraction. The study highlights that heat treatment design, particularly partitioning temperature, must be tailored to the specific steel composition due to the varying effects of Si and Al.
metallurgy & metallurgical engineering