Abstract:In order to investigate the effect of TiB2 contents on the microstructure and wear resistance of titanium matrix composites, commercial pure Ti (CP-Ti) powders with 0–7.5 wt.% TiB2 particles were melted by selective laser melting (SLM) to produce the in-situ Ti-TiB composites. When the TiB2 content increases from 2.5 wt.% to 7.5 wt.%, the microstructures of the Ti-TiB composites undergo a transition from the single phase of α′-Ti to the mixed phases of α′-Ti, TiB and TiB2, and the acicular α′-Ti is refined significantly from 1.03 ± 0.24 μm to 0.36 ± 0.05 μm, showing that increasing the TiB2 content induces the formation of TiB and refines the microstructure. Moreover, large TiB2 particles are not melted completely and they react with the Ti matrix liquid to form a TiB layer around the Ti matrix during SLM. However, small TiB2 particles are completely dissolved into the Ti matrix liquid so that the eutectic TiB grains are precipitated at the boundaries of the Ti matrix after in-situ reaction of TiB2 with Ti. The formation of α′ martensite in the titanium matrix and the addition of TiB2 can induce the fine grain strengthening, the dispersion strengthening, the solid solution strengthening in the SLM-produced composites. The results indicate that the microhardness of the composites increases from 258 ± 10.3 HV0.2 to 435 ± 14.7 HV0.2. The wear process of the SLM-produced CP-Ti and TiB2 reinforced Ti matrix composites is accompanied by adhesion wear, abrasive wear and oxidation wear. As a result, when the TiB2 content increases to 7.5%, the wear resistance of the composites increases by 32.6% compared with that of the CP-Ti. These improvements are mainly due to strengthening and hardening effects induced by TiB2 particles and refinement of Ti matrix. This study provides some basis for developing wear-resistant and high-strength titanium alloys.

Heat Treatment Behaviour of SLM-Built Titanium Matrix Composite: Microstructure and Tribological Performance

Microstructure and Wear-resistant Properties of in situ TiB-TiC Reinforced Titanium Matrix Composites by Laser Deposition Manufacturing

High Temperature Tensile Properties of in Situ TiBw/Ti6Al4V Composites with a Novel Network Reinforcement Architecture

Achieving near equiaxed α-Ti grains and significantly improved plasticity via heat treatment of TiB reinforced titanium matrix composite manufactured by selective laser melting

Constructing Near-Network Microstructure via Heat Treatment for Synergistic Enhancement of Strength and Toughness in (TiB + TiC + La2O3)/TC4 Composite

The Heat Treatment Influence on the Microstructure and Hardness of TC4 Titanium Alloy Manufactured via Selective Laser Melting

Effect of heat treatment on microstructure, mechanical and tribological properties of in-situ (TiC+TiB)/TC4 composites by casting

Construction of Three-Dimensional Network Morphology Titanium Matrix Composites Via Adding Nano B4C: As-built and Heat-Treated Scenarios

Influence of Annealing Heat Treatment on the Microstructure and Mechanical Properties of Multilayer 316L-TiC Composite Fabricated by Selective Laser Melting

High-Temperature Tribology of Selective Laser-Melted Titanium Alloys: Role of Adhesive Wear

Influence of Heat Treatment on the Microstructure and Mechanical Properties of TC4 Alloy Fabricated by Selective Laser Melting

Heat-treatment induced microstructural evolution and enhanced mechanical property of selective laser melted near β Ti-5Al-5Mo-5 V-3Cr-1Zr alloy

Refined microstructure and enhanced wear resistance of titanium matrix composites produced by selective laser melting

Thermomechanical Processing of a Near-α Ti Matrix Composite Reinforced by TiBw

From gradient to homogenous: thermal behavior-induced microstructure evolution and mechanical properties of selective laser-melted TiB2p/2024Al composite

Investigation of Mechanical and Tribological Properties of Al6061–TiB2 Metal Matrix Composites

Wear Behavior of Ti6Al4V Based Hybrid Composites Reinforced with TiB2(7.5%) + TiC (7.5%)

Impact of Heat Treatment on Wear Characteristics of Solid-Lubricated Sillimanite-Ilmenite Aluminum Matrix Composite

Effect of Subtransus Heat Treatment on the Microstructure and Mechanical Properties of Additively Manufactured Ti-6Al-4V Alloy

Microstructure and mechanical properties of (TiB+TiC)/Ti composites fabricated in situ via selective laser melting of Ti and B4C powders

Influence of heat treatment on the microstructure, mechanical and tribological performances of particle reinforced aluminum matrix surface composite fabricated through friction stir processing