Abstract:Objective:To investigate the effect of a porous calcium phosphate/bone matrix gelatin (BMG) composite cement (hereinafter referred to as the "porous composite cement") for repairing lumbar vertebral bone defect in a rabbit model. Methods:BMG was extracted from adult New Zealand rabbits according to the Urist's method. Poly (lactic-co-glycolic) acid (PLGA) microsphere was prepared by W/O/W double emulsion method. The porous composite cement was developed by using calcium phosphate cement (CPC) composited with BMG and PLGA microsphere. The physicochemical characterizations of the porous composite cement were assessed by anti-washout property, porosity, and biomechanical experiment, also compared with the CPC. Thirty 2-month-old New Zealand rabbits were used to construct vertebral bone defect at L 3 in size of 4 mm×3 mm×3 mm. Then, the bone defect was repaired with porous composite cement (experimental group, n=15) or CPC (control group, n=15). At 4, 8, and 12 weeks after implantation, each bone specimen was assessed by X-ray films for bone fusion, micro-CT for bone mineral density (BMD), bone volume fraction (BVF), trabecular thickness (Tb. Th.), trabecular number (Tb.N.), and trabecular spacing (Tb. Sp.), and histological section with toluidine blue staining for new-born bone formation. Results:The study demonstrated well anti-washout property in 2 groups. The porous composite cement has 55.06%±1.18% of porosity and (51.63±6.73) MPa of compressive strength. The CPC has 49.38%±1.75% of porosity and (63.34±3.27) MPa of compressive strength. There were significant differences in porosity and compressive strength between different cements ( t=4.254, P=0.006; t=2.476, P=0.034). X-ray films revealed that the zone between the cement and host bone gradually blurred with the time extending. At 12 weeks after implantation, the zone was disappeared in the experimental group, but clear in the control group. There were significant differences in BMD, BVF, Tb. Th., Tb. N., and Tb. Sp. between 2 groups at each time point ( P<0.05). Histological observation revealed that there was new-born bone in the cement with the time extending in 2 groups. Among them, bony connection was observed between the new-born bone and the host in the experimental group, which was prior to the control group. Conclusion:The porous composite cement has dual bioactivity of osteoinductivity and osteoconductivity, which are effective to promote bone defect healing and reconstruction.

The Ability of Biodegradable Thermosensitive Hydrogel Composite Calcium-Silicon-Based Bioactive Bone Cement in Promoting Osteogenesis and Repairing Rabbit Distal Femoral Defects

Experiment of Porous Calcium Phosphate/bone Matrix Gelatin Composite Cement for Repairing Lumbar Vertebral Bone Defect in Rabbit

Composition control in biphasic silicate microspheres on stimulating new bone regeneration and repair of osteoporotic femoral bone defect

An Injectable, Biodegradable Calcium Phosphate Cement Containing Poly Lactic-Co-glycolic Acid As a Bone Substitute in Ex Vivo Human Vertebral Compression Fracture and Rabbit Bone Defect Models.

A Biodegradable Magnesium Phosphate Cement Incorporating Chitosan and Rhbmp-2 Designed for Bone Defect Repair

Preparation of New Tissue Engineering Bone-Cpc/plga Composite and Its Application in Animal Bone Defects

Injectable Self-Setting Ternary Calcium-Based Bone Cement Promotes Bone Repair

Evaluation of a Biodegradable Graft Substitute in Rabbit Bone Defect Model

Novel highly bioactive and biodegradable gypsum/calcium silicate composite bone cements: from physicochemical characteristics to in vivo aspects

Novel Bioactive Glass Based Injectable Bone Cement with Improved Osteoinductivity and Its in Vivo Evaluation.

Injectable Biocomposites For Bone Healing In Rabbit Femoral Condyle Defects

Synthesis and Characterization of an Injectable and Hydrophilous Expandable Bone Cement Based on Poly(methyl Methacrylate).

A Composite Hydrogel Functionalized by Borosilicate Bioactive Glasses and VEGF for Critical-Size Bone Regeneration

Developing a biodegradable tricalcium silicate/glucono-delta-lactone/calcium sulfate dihydrate composite cement with high preliminary mechanical property for bone filling

Fabricating biodegradable calcium phosphate/calcium sulfate cement reinforced with cellulose: in vitro and in vivo studies

[Physicochemical and Sustained Drug Release Properties of Calcium Phosphate Cement/amifostine/cisplatin Complex and Its Effect in Repairing Bone Defect Due to Tumor Resection in Rabbits].

An injectable pH neutral bioactive glass-based bone cement with suitable bone regeneration ability

Restoration of Critical Defects in the Rabbit Mandible Using Osteoblasts and Vascular Endothelial Cells Co-Cultured with Vascular Stent-Loaded Nano-Composite Scaffolds.

Bioactive composite hydrogel with effects of robust promoting osteogenesis and immunomodulation for osteoporotic bone regeneration

Preparation of 3D Printing PLGA Scaffold with BMP-9 and P-15 Peptide Hydrogel and Its Application in the Treatment of Bone Defects in Rabbits

Improving bone repair of femoral and radial defects in rabbit by incorporating PRP into PLGA/CPC composite scaffold with unidirectional pore structure.