Abstract:During the operation of a steam turbine, its structural elements are subjected to significant thermal and mechanical loads. The consequence of the long-term effect of such a load is the accumulation of scattered fatigue damage to the material of the structural elements of the steam turbine, which is localized over time in the form of fatigue cracks of various types. Evidence of this is several accidents and catastrophic failures of steam turbines due to significant fatigue damage to the shafting. The localization of damage in turbine rotors is facilitated by stress concentration in the gouges and fillets, as well as damage to the surface layer of the rotors during the thermomechanical treatment stage since all metal processing operations (forging, turning and milling, heat treatment) are accompanied by plastic deformation of the material. One of the reasons for the long-term accumulation of fatigue damage in the structural elements of steam turbines is thermal stresses, which can reach dangerous values during turbine startup operations. In certain parts of the rotors, these stresses are sufficient to cause scattered fatigue damage to the material (the so-called thermoplasticity), especially when starting the turbine from a cold state. In the case of crack initiation, the thermal stresses are all the more sufficient for its further intensive development even when starting the turbine from uncooled and hot states, which are less damaging than starting from the cold state. To study the intensity of crack growth in the turbine rotor due to thermal stresses arising during turbine startup, a computational model based on using a finite element model of the shaft of the K-200-130 steam turbine and fracture mechanics approaches is proposed. Studies based on the proposed computational model have demonstrated the ability to predict the process of crack growth in the rotor due to turbine startup from different thermal states and assess its danger to structural integrity. The initial size of the internal annular crack was determined, which has the potential for further intensive growth under the influence of thermal stresses.

The effect of dwell times and minimum temperature on out-of-phase thermomechanical fatigue crack propagation in a steam turbine steel—Crack closure prediction

Fatigue Crack Propagation Analysis in an Aero-Engine Turbine Disc Using Computational Methods and Spin Test

Effect of Microstructure on Fatigue Crack Propagation Behavior in a Steam Turbine Rotor Steel

Out-of-phase thermo-mechanical fatigue crack growth and the effect of the compressive minimum load level on crack closure at notches

Evaluation of the Effect of Various Prior Creep-Fatigue Interaction Damages on Subsequent Tensile and Creep Properties of 9%cr Steel

Research on Microstructure Dependence of Near-Threshold Fatigue Crack Propagation by Combined Analyses of Fracture Surface and Fatigue Crack Growth Path

Influence of High-Temperature Dwell Time on Creep-Fatigue Behavior in A 1000 Mw Steam Turbine Rotor

Couple effects of temperature and fatigue, creep-fatigue interaction and thermo-mechanical loading conditions on crack growth rate of nickel-based alloy

Effect of sustained load on fatigue crack growth behavior of FGH96 at elevated temperature

Estimation of Fatigue Crack Growth at Transverse Vibrations of a Steam Turbine Shaft

The Effect of Stress Ratios on the Very High Cycle Fatigue Behavior of 9%Cr Turbine Steel at 630 °C

Effect of Solution Annealing on Fatigue Crack Propagation in the AISI 304L TRIP Steel

Development of Analogy Method for Thermal-Fatigue Crack Propagation in Pressurized Cylinder by Using Permeation Diffusion-Fracture Model

On the Creep Fatigue and Creep Rupture Behaviours of 9–12% Cr Steam Turbine Rotor

Deformation and Damage Behavior of a 1Cr-Cast Steel Under Multiaxial Loading at Elevated Temperatures

Corrosion-Fatigue Prediction Methodology for 12% Cr Steam Turbine Blades

Effect of microstructure on the fatigue crack growth behavior of 9%Cr martensitic steel at different stress ratios under 630 °C

Micromechanical Finite Element Modelling of Thermo-Mechanical Fatigue for P91 Steels

An Analytical Study on Cracking Directions and Damage in Thermal Fatigue Crazing Subjected to Variable Amplitude Loadings

Experimental and Numerical Studies on Fatigue Crack Propagation of Surface Cracks in Heat-Resistant Steel CrMoCoV Considering Closure Effect

Patterns of Growth of an Internal Annular Crack Under the Influence of Thermal Stresses During Turbine Startup