Abstract:AlxNb0.5TiV2Zr0.5 (x = 0, 0.2, 0.4, 0.6, 0.8, 1.0) refractory high entropy alloys were prepared by vacuum arc melting to obtain a lightweight REHA with excellent microstructure and mechanical properties. The microstructure, density, hardness, and compressive properties at room and elevated temperatures of AlxNb0.5TiV2Zr0.5 alloys were investigated. All AlxNb0.5TiV2Zr0.5 alloys are composed of the BCC phase and the C14-Laves phase, and the volume fraction of the Laves phase raises from 12.03% to 22.83% and then decreases slightly to 20.31% with the increase of Al content. The density of AlxNb0.5TiV2Zr0.5 alloys decreases with the increase of Al content from 6.12 g/cm3 to 5.43 g/cm3, and the microhardness increases from 397.2 HV to 641.9 HV. At room temperature, the yield strength of AlxNb0.5TiV2Zr0.5 alloys increases obviously at first and then decreases slightly with the range of 843 MPa–1727 MPa. The compressive strain of the alloys obviously decreases from 33.4% to 13.7% at first and then increases to 16.6%. Upon increasing the temperature to 873 and 1073 K, the strength of all alloys decreases, and the yield strength of the Al0.8 alloy remains 1569 and 1108 MPa, respectively. The compression ratios of all AlxNb0.5TiV2Zr0.5 alloys reach 50% without fracture at this temperature. The specific yield strength of Al0.8 alloy acheives 312 × 103, 284 × 103, and 199 × 103 MPa·cm3g-1 at 298, 873, and 1073 K, which is superior to that of other alloys. A strong correlation between the mechanical properties and the Al content of AlxNb0.5TiV2Zr0.5 alloys is observed. Al is one of the elements that can promote the formation of the Laves phase, and the volume fraction of the Laves phase increases with the increasing Al content. As a hard intermetallic compound phase, the mechanical properties of the alloys are improved with the increasing volume fraction of the Laves phase.

Synthesis of High-Entropy Alloy AlTiZrVNb by Aluminothermic Reaction

Aluminothermic synthesis of high entropy alloys from metals of IV and V groups

Possibility of obtaining refractory high-entropy AlTiZrVNb alloys from metal oxides

Investigation of the formation and distribution of elements in the production of Al-Ti-V-Zr-Nb alloys by the aluminothermic method

Microstructure and elevated-temperature mechanical properties of refractory AlMo0.5NbTa0.5TiZr High Entropy Alloy fabricated by powder metallurgy

SYNTHESIS AND STRUCTURE OF FOUR TiZrVNb AND FIVE-COMPONENT TiZrHfVNb REFRACTORY HIGH-ENTROPY ALLOYS

A single-phase bcc high-entropy alloy in the refractory Zr-Nb-Ti-V-Hf system

Enhanced High-Temperature Strength of HfNbTaTiZrV Refractory High-Entropy Alloys by AI 2O 3 Reinforcement

In-Situ Alloy Formation of a WMoTaNbV Refractory Metal High Entropy Alloy by Laser Powder Bed Fusion (PBF-LB/M)

Microstructure and tribological properties of TiZrV0.5Nb0.5Al refractory high entropy alloys at elevated temperature

Oxidation resistance of Al-containing refractory high-entropy alloys

Simultaneously enhanced oxidation resistance and mechanical properties in a novel lightweight Ti2VZrNb0.5Al0.5 high-entropy alloy

Achieving exceptional high-temperature strength and oxidation resistance in an additively manufactured refractory high-entropy alloy via strategic elemental substitutions

Microstructure, Mechanical Properties and Corrosion Resistance of the Mo0.5V0.5NbTiZrx High-Entropy Alloys with Low Thermal Neutron Sections

A novel lightweight refractory high-entropy alloy

Investigation of the features of phase formation in the joint aluminothermic reduction of ZrO2, Ta2O5, Nb2O5

Thermal Stability of Microstructure of High-Entropy Alloys Based on Refractory Metals Hf, Nb, Ta, Ti, V, and Zr

Effect of Al on microstructure and mechanical properties of lightweight AlxNb0.5TiV2Zr0.5 refractory high entropy alloys

Effect of the Synthesis Route on the Microstructure of HfxTi(1−x)NbVZr Refractory High-Entropy Alloys

Production of Nb-Zr alloy by aluminothermic reduction-electron beam refining 1st Report. Fundamental Study of Aluminothermic Reduction of Niobium Oxide and Zirconium Oxide.

High entropy alloy MoNbTaVW synthesized by metal-oxide reduction in a microwave plasma