Abstract:In this paper, a new process for the phase-separated P2O5-Al2O3 glass with SiO2-rich region is presented. The new method combines pneumatic atomization with mechanical stirring based on melting-quenching preparation. X-ray diffraction, Nano-infrared spectra, X-ray photoelectron spectra, Raman scattering spectra and atomic force microscope were carried out to investigate sample's structure and surface morphology. The results show that the phase-separated glasses consist of second phase, transition region and matrix region. The average diameter of separated phase, ie. 500 nm, 150 nm, 76 nm and 85 nm, depends on the diameter of SiO2 glass particles prepared by ball milling, that is 50 mu m, 10 mu m, 2 mu m and 400 nm respectively. Especially, transition region is formed by the connection of phosphorus oxygen tetrahedron and silicon oxygen tetrahedron, located between SiO2 region and matrix network region. After introducing the second phase, the Young's modulus of matrix glass was increased by 32.5% and the optimal value is 77.67 GPa within the scope of this experiment. It is attributed to that the formation of transition region increases the cross-linking of P2O5-Al2O3 glass network. The Young's modulus of the phase-separated glass increases with the diameter of the quartz glass particles decreases from 50 mu m to 2 mu m, but weakens at a diameter of 400 nm. The network polymerization due to increasing in the number of P3 units induced by second phase's diameter is responsible for rising in the Young's modulus, whereas too low diameter leads to particle agglomeration accompanied by the present of defects.

New approach for preparation of high-purity sulfide-germanium glasses doped with praseodymium

Preparation of high-purity germanium telluride based glasses with low oxygen impurity content

Preparation of high purity glasses in the Ga–Ge–As–Se system

Preparation of high purity glasses based on germanium and gallium tellurides using chemical transport

Sol–gel preparation of Ge nanocrystals embedded in SiO2 glasses

Synthesis and Characterization of Chloro-Sulphide Glass-Ceramics Containing Neodymium(Iii) Ions

Preparation and Luminescence of New Nd3+ Doped Chloro-Sulphide Glass–ceramics

Rare earth elements as a source of impurities in doped chalcogenide glasses

Preparation and investigation of high purity Ge–Te–AgI glasses for optical application

Germanium Doping of Si Substrates for Improved Device Characteristics and Yield

A Novel Method for Preparing Phase-Separated P2O5–Al2O3 Glass with High Young's Modulus

Amorphous silica containers for germanium ultrapurification by zone refining

The Ability of GexGa4S96-x Chalcogenide Glasses Dissolving Rare Earth Probed by X-Ray Photoelectron Spectra Analysis

Synthesis and Spectroscopy of High Concentration Dysprosium Doped Ges2-Ga2s3-Cdi2 Chalcohalide Glasses and Fiber Fabrication

Preparation of rare-earth aluminate glasses by powder sintering and nano-ceramics by glass crystallization: A mini-review

Elimination of impurities in Ge-Se-Sb glasses

Investigation on gallium doping Ge-As-S chalcogenide glass and glass ceramics

Hybrid Molecular Beam Epitaxy of Ge-based Oxides

Preparation and Characterization of Oxychalcogenide Ngese_2-Geo_2 Glasses