Abstract:In this paper, We prepared two groups of the glasses, the first group is Ge x As 20 Se 80-x with x from 5 % to 32.5 %, the second group is Ge x Sb 20 Se 80-x with x from 5 % to 25 %, using the conventional melt-quench method, and investigated the effect of the elemental substitution of As by Sb on the threshold behaviors in Ge x As(Sb) 20 Se 80-x glasses. We aimed to understand that,to which degree the topological model and chemical order model can explain the correlation between the physical properties and glass compositions, and how the chemical composition can affect the transition threshold in the glasses. Glass transition temperature was measured by the differential scanning calorimeter (Mettler-Toledo, DSC1) with different scanning rates from 5 K/min to 30 K/min under a uniform nitrogen gas flow of 50 mL/min, the density of the glasses was measured by a Mettler H20 balance with a MgO crystal used as a reference. Samples from each glass composition were weighed five times and the average density was recorded, the refractive index of the glass at 1.5 um was measured by a Metricon Model 2010 prism coupler. Raman spectra were measured from a T64000 Jobin-Yvon-Horiba micro-Raman spectrometer equipped with a liquid-nitrogen-cooled CCD detector. The 830 nm laser line was used as an excitation source, and the laser power was kept as small as possible to avoid any photo-induced effects. The resolution of the spectrometer was about 0.5 cm -1 . The result from systematic measurements of these physical parameters shows that, while the transition thresholds at MCN=2.4 and 2.67 were verified in the Ge-As-Se glasses with ideal covalent network, these two transitions represent the covalent network structure inside the glass from an under-constrained “floppy” network to an over-constrained “rigid” phase and from the two-dimensional to the three-dimensional “stressed rigid” phase respectively. However, when As is substituted by Sb, the Ge x Sb 20 Se 80-x glass with non-ideal covalent network will change of the transition thresholds, which changes to the chemically stoichiometric composition. We further deconvolved Raman scattering spectra into different structural units and the change of their respective intensity showed the same behavior, and this was ascribed to the chemical effect induced by a large difference of the atomic radius between As and Sb, and a relatively strong ionic feature of the element Sb.

Elimination of impurities in Ge-Se-Sb glasses

Thermal and Optical Properties of the Ga–Ge–Sb–Se Glasses

Chalcogenide Coatings of Ge_15Sb_20S_65 and Te_20As_30Se_50

Preparation of high purity glasses in the Ga–Ge–As–Se system

Study of Effects of Te Addition and Oxygen Contamination on the Surface Short Range Order Structure of GeBiSe Glass by XPS

Iodine-doped Ge-As-Se glasses with high purity and low dispersion

IR impurity absorption in GeS2-In2S3-AgI chalcohalide glasses

Effect of Annealing Conditions on the Physio-Chemical Properties of Spin-Coated As2se3 Chalcogenide Glass Films

Effect of the elemental substitution on threshold behaviours in Ge-As(Sb)-Se glasses

FORMATION OF GeSe2-As2 Se3-CdSe INFRARED GLASSES

Micro-crystallization of the Infrared Transmitting Chalcogenide Glass in GeSe2–As2Se3–PbSe System

Preparation of high-purity germanium telluride based glasses with low oxygen impurity content

Preparation and investigation of high purity Ge–Te–AgI glasses for optical application

Effect of CsI Addition on the Thermal Properties, Crystallization Kinetics and Short-Wavelength Absorption Edges of GeSe2–Ga2Se3 Glasses

Formation and Properties of GeSe2–Ga2Se3–PbI2 Novel Chalcohalide Glasses

Rare earth elements as a source of impurities in doped chalcogenide glasses

Glass formation and optical properties of Sn modified GeS2-Ga2S3-CsCl chalcogenide glasses

Effects of the Se Substitution for Te on the Structure and Properties of Glasses in the Ag30As28(SexTe100-x)42 System

The Effects of Germanium Addition on Properties of Ga-Sb-S Chalcogenide Glasses

Impact of impurities on the thermal properties of a Li2S–SiS2–LiPO3 glass