Abstract:We report herein a typical piezoelectric polymer, poly(vinylidene fluoride) (PVDF) to be successfully wrapped on single-walled carbon nanotubes (SWCNTs) using a simple supercritical carbon dioxide (SC CO(2)) antisolvent-induced polymer epitaxy method. Our study focused on the effect of different solvents on the morphology of PVDF wrapping on SWCNTs. Three organic solvents, dimethyl sulfoxide (DMSO), N,N-dimethylformamide (DMF), and N,N-dimethylacetamide (DMAc) were chosen for PVDF. When DMSO was used as solvent, the decorating degree of PVDF on the surface of SWCNTs increases significantly with the increase of SC CO(2) pressure, and nanocrystals wrapping on SWCNTs can be observed at high pressure. FTIR and Raman spectra indicated that there exist interactions between SWCNTs and PVDF chains. What's more, FTIR results also show that there exists a transformation from the beta-phase to the alpha-phase of PVDF in DMSO with the assistance of SC CO(2), which is similar to the action of elongation/shear flow field. It indicated that the alpha-phase is the predominant form occurring on the surface of SWCNTs after treatment with SC CO(2). And the helical structure on SWCNTs observed from the TEM image reflected the alternate trans- and gauche-bond conformation of the alpha-form. When DMF or DMAc was used as the solvent, although nanocrystal wrapping and helical structure was not visible, the samples had more excellent dispersion than that in DMSO. Particularly, for DMF, a typical network structure was observed, which is similar to a spider web. Therefore, this work supplies a clue that the various morphologies of nanohybrid structure can be obtained just by changing the solvent during the treatment process of SC CO(2), and accordingly, the tailored nanohybrid structure are promising and important for functional design as a basic component in microfabrication and other fields.

Selective dispersion of semiconducting single-walled carbon nanotubes with aromatic polyimides

Electrical property-selective noncovalent dispersion of carbon nanotubes by poly(perylene diimide-thiophene): a molecular dynamics study

Enhancing dispersion of copper nanowires in melt-mixed polystyrene composites

Single-walled Carbon Nanotube–polymer Composites: Electrical, Optical and Structural Investigation

Polymer Structure and Solvent Effects on the Selective Dispersion of Single-Walled Carbon Nanotubes

Diketopyrrolopyrrole (Dpp)-Based Donor-Acceptor Polymers for Selective Dispersion of Large-Diameter Semiconducting Carbon Nanotubes.

Enhanced Dispersion of Nanotubes in Organic Solvents by Donor-Acceptor Interaction Between Functionalized Poly(Phenylacetylene) Chains and Carbon Nanotube Walls

Di-thiafulvalene functionalized phenylene acetylene-polymers for selective dispersion of single walled carbon nanotubes (SWNTs)

Selective Synthesis Combined with Chemical Separation of Single-Walled Carbon Nanotubes for Chirality Selection

Synthesis of Asymmetric Imine Polymers for Highly Selective Sorting of Semiconducting Single-Walled Carbon Nanotubes by Two in One Strategy

Selective Dispersion of Large‐Diameter Semiconducting Carbon Nanotubes by Functionalized Conjugated Dendritic Oligothiophenes for Use in Printed Thin Film Transistors

Composites Of Functional Poly(Phenylacetylene)S And Single-Walled Carbon Nanotubes: Preparation, Dispersion, And Near Infrared Photoresponsive Properties

Separation of Semiconducting Carbon Nanotubes Using Conjugated Polymer Wrapping

Dispersant Selection for Nanomaterials: Insight into Dispersing Functionalized Carbon Nanotubes by Small Polar Aromatic Organic Molecules

Surfactant Assisted Dispersion of Single-Walled Carbon Nanotubes in Polyvinylpyrrolidone Solutions

Electrical Properties Of Single-Wall Carbon Nanotube-Polymer Composite Films

Effect of the selective localization of carbon nanotubes and phase domain in immiscible blends on tunable microwave dielectric properties

Conjugated Polymer-Controlled Selective Dispersion of Single-Walled Carbon Nanotubes and Fabrication of Network Transistors

Modification of carbon nanotubes using poly(vinylidene fluoride) with assistance of supercritical carbon dioxide: the impact of solvent

Why semiconducting single-walled carbon nanotubes are separated from their metallic counterparts.

Why Semiconducting Single-Watted Carbon Nanotubes Are Separated From Their Metaltic Counterparts