Optimum conditions for quantitative analysis of beryllium by electron probe microanalysis: A case study of beryl
Wenlan Zhang,Xudong Che,Rucheng Wang,Lei Xie,Xiaofeng Li,Di Zhang
DOI: https://doi.org/10.1360/tb-2020-0316
2020-06-02
Chinese Science Bulletin
Abstract:Beryllium (Be) is resistant to high temperatures and corrosion, and thus is an important strategic resource for use in defense and military industries. Beryllium is also used in nuclear reactors as a neutron reflector or moderator. At present, there are numerous unresolved research questions regarding Be resources, including the mechanisms of Be mineralization, Be occurrence in minerals, and Be separation and extraction from ores. Therefore, it is important to be able to measure Be contents of minerals in situ by electron probe microanalysis (EPMA). However, given that Be is an ultra-light element, it is the most difficult element to measure by EPMA. The objectives of this research were to: (1) develop robust techniques for EPMA of Be-bearing minerals to support research into Be resources; and (2) advance the techniques for the measurement of ultra-light elements. In this study, beryl samples from the Xuebaoding deposit in Sichuan Province, China, were selected for Be analysis by EPMA. Data from two different electron microprobes (JEOL JXA-8800 and JXA-8100) with different crystals (LDEB and LDE3H, respectively) were compared. Our results show that the LDE3H crystal is better for Be analysis than the LDEB crystal, as the interplanar spacing of the former (2d=20 nm) is much larger than that of the latter (2d=14 nm). Under appropriate measurement conditions, satisfactory Be data can be obtained with the LDE3H crystal. The highest peak count for the Be Kа line in the Be metal sample was obtained at an accelerating voltage of 10 kV (higher than at 3, 5, or 15 kV). The highest peak-to-background ratio for the Be Kа line in the beryl sample was also obtained at an accelerating voltage of 10 kV , a probe current of 100 nA, and beam size of 10 µm. The highest peak-to-background ratio for the Be Kа line in the beryl sample was obtained at a probe current of 20 nA (higher than at 10, 50, 100, or 200 nA) with an accelerating voltage of 10 kV and beam size of 10 µm. Thus, the optimum analytical conditions are as follows: accelerating voltage=10 kV; beam current=20 nA; beam size=0–10 µm; PHA (gain)=128; base=1; window=5; slit open; differential mode; standard=Be metal; thickness of carbon film for Be metal standard and beryl sample=15 nm; background=avoidance of interference peaks of other elements close to the Be peak position in high order; ZAF correction. Based on the chemical characteristics of Be, we also investigated why Be is challenging to measure by EPMA, and considered the chemical peak shift during analysis and the selection and optimization of the analytical conditions. The peak shifts for different Be minerals are caused mainly by the hybridization of atomic orbits between Be and O atoms. The absorption effect is the main reason why Be analyses are challenging by EPMA. The absorption effect is mainly due to O atoms, as well as other elements in minerals, such as Si, Na, Mg, and Li. A uniformly and accurately controlled carbon film thickness for the standard and samples is a key factor. A digital coating instrument (LEICA-EM-ACE200) was used in this work to ensure a precise finish. A compilation of published Be data obtained with JEOL, Shimadzu, and Cameca EMPA instruments shows that each has different crystals (LDE3H, LSA300, and PC3, respectively) and conditions for optimal Be analysis. In addition, the optimal peak position, accelerating voltage, and beam current vary for different Be Bearing minerals analyzed with the same EPMA instrument. However, a low beam current and accelerating voltage generally minimize the absorption effect on Be.