Abstract:3D woven fabric-reinforced composites (3DWFRCs) offer excellent structural integrity, impact resilience, and strength-to-weight ratios, making them ideal for advanced lightweight engineering applications. The purpose of this research is to investigate the effects of binder yarn pathways, stuffer–binder ratios, and inter-yarn cross-overs on out-of-plane and in-plane impact responses under low-velocity conditions in six different 3D weave structures with a consistent areal density. This study investigated the out-of-plane impact properties of 3DWFRCs across 16–50 J energies, revealing how weave architectures affect damage tolerance, including rebound, penetration, and perforation thresholds. The orthogonal matt 3×3 (4SLORMT3) weave, with the fewest inter-yarn cross-over points, demonstrated superior low-velocity impact performance, highlighting the crucial role of nonlinear inter-yarn friction dynamics in enhancing composite impact resistance. A parallel trend was observed in the through-thickness angle-interlock weave structures, with 4SLANTW (angle-interlock twill 3×3) outperforming 4SLANPL (angle-interlock plain 1×1), attributed to its elongated binder yarn float length and fewer inter-yarn cross-over points. An X-ray micro-computed tomography scan was used for non-destructive testing to measure impact toughness and demonstrate the extent of damage resulting from a projectile impact at 3.14 m/s. Furthermore, compression-after-Impact tests were carried out on those perforated specimens, to provide a comprehensive evaluation of their damage tolerance. When subjected to a pendulum impact at 3.54 m/s and 11 J, the 4SLORPL weave, which has 350 inter-yarn cross-over points, exhibits exceptional resistance to edgewise impact force. This is attributed to the heightened inter-yarn friction, which accentuates energy dissipation and facilitates effective stress distribution.

Effect of yarns in multiple directions on impact resistance of aramid/epoxy composites

Impact response and damage evolution of triaxial braided carbon/epoxy composites. Part I: Ballistic impact testing

The Effect of Single and Double-wefted Styles on the In-plane Impact Behavior of Fabric Carbon-aramid/Epoxy Intralayer Hybrid Composite Laminates

Low-velocity impact performance of ultra-high molecular weight polyethylene/aramid-polyester core-spun yarn hybrid composites

Effect of woven yarn angle on the low‐velocity impact damage response of fibre woven thermoplastic composites

Mechanical Characterization and Impact Damage Assessment of Hybrid Three-Dimensional Five-Directional Composites

Impact Performance of 3D Orthogonal Woven Composites: A Finite Element Study on Structural Parameters

An experimental investigation on the influence of weave architectures on out-of-plane and in-plane impact properties of 3D woven fabric-reinforced composites

Effect of Yarn Reduction Types on the Mechanical Response and Damage Mechanism of 3D Woven Composites Subjected to Low-velocity Impact

X-ray microtomography analysis of the damage mechanisms in 3D circular braided carbon fiber/epoxy resin composite tubes under axial impact compression

Experimental Investigation on Low-Velocity Impact Performance of 3D Woven Textile Composites

Interfacial Interaction in Sisal/Epoxy Composites and Its Influence on Impact Performance

Low-velocity impact response of 3D woven hybrid epoxy composites with carbon and heterocyclic aramid fibres

Low-Velocity Impact and Post-Impact Residual Flexural Properties of Kevlar/EP Three-Dimensional Angle-Interlock Composites

Impact Response of 3D Orthogonal Woven Composites with Different Fiber Types

Analysis of the influence of yarn angle on the mechanical behaviors of cured woven composites

Comparative studies on the effect of fabric structure on mechanical properties of carbon fiber/epoxy composites

Preparation of highly active aramid fiber and effect on the interface property of aramid/epoxy composites

Research on the Influence of Yarn Reduction on the Bending Performance of Three-dimensional Woven Composites

Interfacial studies on the surface modified aramid fiber reinforced epoxy composites

Effects of yarn defects and specimen size on impact compressive damages of 3-D angle interlock woven composites