Abstract:CoMoCrSi coatings with different thickness were prepared by high velocity oxy-fuel spraying (HVOF) and atmospheric plasma spraying (APS), respectively. Variation of microstructure and phase constitution the coatings were investigated by SEM and XRD, respectively. Thermal shock performance of the coatings was evaluated by heating (500 °C and 900 °C) and water quenching method. Compared with APS coatings, the as-sprayed HVOF coatings exhibited denser microstructure and higher hardness. The phase and microstructure of the coatings did not change significantly after 50 thermal cycles at 500 °C. On the contrary, spallation was observed in APS coatings with thickness of ∼350 μm during 900 °C thermal shock cycles. Obvious oxidation appeared in all of the coatings after 900 °C thermal shock. Meanwhile, segmentation cracks perpendicular to the coating surface were found in the edge of 900 °C thermal shocked HVOF coatings (both ∼350 μm and ∼130 μm) and APS coatings (∼350 μm). Element interdiffusion was not detected between the substrate and coating after 50 thermal shocks at 900 °C or 500 °C. After the thermal shock at 500 °C, the microhardness of the ∼130 μm coating did not change greatly while the microhardness of the ∼350 μm coating was greatly improved. After the thermal shock at 900 °C, the microhardness of the coating increased by about 40 % due to the reduction of defects in the coating and the generation of hard phases. At the same time, the migration of elements and the oxidation and recrystallization of some phases may increase the hardness of the coating.

Thermal shock behaviour and failure mechanism of two-kind Cr coatings on non-planar structure

Thermal Shock Behavior of Al2O3/TiO2-NiCrBSi Graded Thermal Barrier Coatings Produced by Flame Spraying

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Failure behavior of Cr coating on PCrNi3MoVA steel under thermal-mechanical factors

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Microstructure evolution and adhesion properties of thick Cr coatings under different thermal shock temperatures

Effects of Heat Treatment on Structure Transformation of Cr/Al Composite Coatings

A study on the mechanical and thermal shock properties of MCrAlY coating prepared by arc ion plating

Structural Characteristics and Evolution in the Crack Propagation Process of NiCrAlY/YSZ Gradient Coatings Through Thermal Shock at 900 °C

Thermal shock resistance of Cr/CrN/Cr/CrAlN multilayer anti-erosion coating

Mechanical property and cracking mechanism of Cr-coated Zr alloy under tensile and compressive loading

Microstructure and electronic structure of Cr2C and Fe2Y in the Cr-coating prepared by pack-cementation on the surface of ODS steel

Effects of Transient Thermal Shock on the Microstructure and Mechanical Properties of CoCrFeNiMn High-Entropy Alloy Coatings

Interface stability and microstructural evolution of the (Cr/CrN)24-coated zirconium alloy under different thermal shock temperatures

Investigations on 1200 °C steam oxidation behavior of Cr coatings with distinct crystallographic orientation on Zircaloy-4 alloys

Mechanical and high-temperature steam oxidation properties of Cr coatings deposited via high-power impulse magnetron sputtering

Microstructure effects on fracture failure mechanism of CrAl/CrAlN coating

Microstructure and thermal shock behavior of CoMoCrSi coatings prepared by HVOF and APS

Influence of atomic migration mode at different temperatures on the microstructure, mechanical and cavitation erosion behaviors of Co-based alloy coating

Effect of annealing on the microstructure, mechanical and electrochemical properties of CrAlC coatings