Abstract:The study particularly focuses on the effect of the Cr co-doping on the structural, optical and magnetic properties of Zn0.99Fe0.01O. Zn0.99-xFe0.01CrxO (x =0, 0.01, 0.03 and 0.05) nanoparticles. Powder x-ray diffraction (XRD) analysis confirms all the samples have hexagonal wurtzite structures. The average crystallite size (D) and microstrain of the samples were calculated using the Williamson-Hall relation and D was found to be 13 +- 1 nm for Zn0.99Fe0.01O. In Cr co-doped samples, D increase slightly with Cr content and are given by 9 +- 1, 10 +- 1, and 11 +- 1 nm for the samples with x = 0.01, 0.03 and 0.05, respectively; while the strain decreased with increase in Cr co-doping. Transmission electron microscopy (TEM) images of the samples indicate that particles are in the nano-regime and agglomerated. Particle sizes are found to be 14 +- 1, 11 +- 1 and 12 +- 1 nm for Zn0.99-xFe0.01CrxO with x = 0, 0.03 and 0.05, respectively. The substitution of Fe3+ and Cr3+ at Zn2+ sites has an impact on the optical properties. The band-gap decreases from 3.296 +- 0.002 eV to 3.258 +- 0.002 eV with increase of Cr concentration. Photoluminescence (PL) of Zn0.96Fe0.01Cr0.03O revealed the presence of defects, the emission peaks at 410 nm and 513 nm are attributed to Zn vacancies (VZn) and singly ionized oxygen vacancies, respectively. The M(-H) curves of Zn0.99-xFe0.01CrxO (x = 0.03 and 0.05) measured at room temperature using a vibrating sample magnetometer (VSM) are found to be hysteretic, signifying room temperature ferromagnetism (RTFM). Maximum saturation magnetization, 0.67 +- 0.01 emu.g-1, is observed in Zn0.94Fe0.01Cr0.05O. The observed RTFM in Fe+Cr co-doped ZnO is explained by of bound magnetic polaron (BMP) mechanism, the BMPs are formed by VZn and Vo^+ defects. This paper enhances the understanding of the origin of RTFM in Fe+Cr co-doped ZnO nanoparticles.

Optical and Magnetic Behaviors of Ru-Doped ZnO Nanoparticles

Zn-doped SnO2 Nanoparticles: Structural, Optical, Dielectric and Magnetic Properties

Zn-Cu-codoped SnO2 Nanoparticles: Structural, Optical, and Ferromagnetic Behaviors

Characterization of ZnO:Co particles prepared by hydrothermal method for room temperature magnetism

The influence of Nd 3+ doping on the structural, optical, magnetic, and dielectric characteristics of nanoscale hexagonal wurtzite type ZnO

Cobalt-doped ZnO nanoparticles and PLD-deposited thin film forms: structure, optical properties and nature of magnetic anisotropy

Tuning the structural, optical and magnetic properties of transition metal doped zinc oxide nanoparticles

Consequence of Mn and Ni doping on structural, optical and magnetic characteristics of ZnO nanopowders: the Williamson–Hall method, the Kramers–Kronig approach and magnetic interactions

Synthesis and thermoelectric properties of RuO2 nanorods

Structural and Magnetic Properties of Zn1−xMnxO (0≤x≤0.40) Nanoparticles

Role of Sp-D Exchange Interactions in Room-Temperature Photoluminescence and Ferromagnetism of CuCo Co-doped ZnO Nanorods.

Experimental and DFT Studies of Structure, Optical and Magnetic Properties of (zn1−2xcexcox)o Nanopowders

Influence of ZnO Codoping on Growth and Holographic Properties of Ru/Fe Double-Doped LiNbO3 Single Crystals

Room-Temperature Ferromagnetism in Cu/Co Co-Doped ZnO Nanoparticles Prepared by the Co-Precipitation Method: For Spintronics Applications

Structure, optical and magnetic properties of Fe doped, Fe+Cr co-doped ZnO nanoparticles

Studying the Effect of Cobalt Doping on Optical and Magnetic Properties of Zinc Oxide Nanoparticles

Energy Gap and Defects Engineered Optical, and Magnetic Properties of ZnO-based Diluted Magnetic Semiconducting Nanoparticles

Oxygen-vacancy-induced Green Emission and Room-Temperature Ferromagnetism in Ni-doped ZnO Nanorods

Optical and magnetic properties of Ni-doped ZnO nanocones.

Band gap and magnetic properties modulation by substitution of cobalt in ZnO nanostructures

Impact of Cr doping on the structure, optical and magnetic properties of nanocrystalline ZnO particles