HgI2@CsI core/shell nanoparticles: Synthesis, characterization, and application in photosensors
Amnah S. Abd-Alrahman,Raid A. Ismail,Mudhafar A. Mohammed
DOI: https://doi.org/10.1016/j.jics.2022.100515
IF: 0.243
2022-07-01
Journal of the Indian Chemical Society
Abstract:Due to their excellent characteristics such as carrier transport ability, high electrical conductivity, and mobility, core/shell nanostructure photovoltaic devices have received a lot of interest. In this study, HgI2@CsI core/shell nanoparticles were synthesized by using two-step pulsed laser ablation in liquid (PLAL) at laser fluences of 12.7 and 33.1 J/cm2. The structural and optical properties of the samples were examined using X-ray diffraction (XRD), zeta potential (ZP), energy dispersive X-ray (EDX), transmission electron microscope (TEM), UV–Vis absorption, and photoluminescence spectra. The XRD data conforms to the formation of cubic CsI and tetrahedral and orthorhombic HgI2. The zeta potential results show that the sample prepared at 33.1 J/cm2 has the highest stability. TEM images show the formation of core-shell morphology and the thickness of the shell depends on the laser fluence. UV–Vis results show that the band gap of the core/shell was 3.22 and 3.23 eV for 12.7 and 33.1 J/cm2, respectively. The fluorescence spectra show two emission peaks for two laser fluences. The current-voltage characteristics of the HgI2@CsI/Si heterojunction were measured at dark and illumination, and the maximum On/Off ratio was about 167 for a photodetector prepared at 12.7 J/cm2. The figures of merit of the photodetectors, including responsivity, external quantum efficiency, and detectivity, are measured at room temperature. A responsivity as high as 0.7 W/A at 400 nm was obtained for a photodetector fabricated at 12.7 J/cm2.
chemistry, multidisciplinary