Abstract:Powdered Ni-based catalysts exhibit good performance in the dry reforming of methane (DRM); however, they suffer from limited industrial applicability. Structured monolithic catalysts can overcome these limitations. In this sense, we present the synthesis of Ni–Ce mixed oxide-type catalysts immobilized in cordierite monoliths using a simple coprecipitation method and slurry coating without additives using hydrotalcite precursors for catalyst preparation. Our research explores the role of Ce (0–7 % w/w) as a promoter and the impact of immobilizing mixed oxides (MO) within cordierite monoliths on the physicochemical properties and catalytic performance of non-previously H 2 -reduced materials in DRM at 700 °C. Our findings reveal the favorable impact of Ce on the physicochemical properties of the catalyst in both the powder and monoliths, including smaller crystallite sizes, enhanced CO 2 adsorption, and reducibility with higher Ce loading. The immobilized mixed oxide (MO) maintained its crystalline structure and formed stable, uniform layers with thicknesses below 10 μm in the monoliths. The powders exhibited stable conversions of 70–80% for CH 4 and 66–75% for CO 2 , whereas the monoliths showed conversions of 85–90% for CH 4 and 80–90% for CO 2 at 700 °C and 94,680 mL·g cat −1 ·h −1 . A higher catalyst loading in the monoliths did not result in detrimental catalytic conversion. On average, the monoliths had a higher H 2 /CO ratio (1.25–1.5) compared to the powders (1–1.25), which may explain the increased coke formation rate in the monoliths from methane cracking. Ce improved the stability and reduced coke formation, particularly when the space velocity was lower. This research highlights the significant advantages of immobilizing mixed oxides (MO) in monolithic structures, making them highly promising for potential industrial scale-up. Their stability, recoverability, elimination of high-cost H 2 reduction, and reusability in subsequent catalytic tests contributed to their favorable characteristics.

Ni/CeO2 Catalyst Prepared via Microimpinging Stream Reactor with High Catalytic Performance for CO2 Dry Reforming Methane

Co–Ni Alloy Supported on CeO2 As a Bimetallic Catalyst for Dry Reforming of Methane

Preparing a Zr-Doped CeO 2 Nanorod to Improve the Catalytic Performance of the Ni-Based Catalyst for Dry Reforming of Methane by Enhancing Oxygen Supply

Self-Confinement Created for a Uniform Ir–Ni/SiO2 Catalyst with Enhanced Performances on CO2 Reforming of Methane

Improving the anti-coking ability in the Ni-M(M = Ce, Zr, Co)@SiO 2 yolk-shell catalysts for dry reforming of methane

Immobilization of Ni on MOF-derived CeO 2 for promoting low-temperature dry reforming of methane

Lamellar cross-linking Ni/CeO 2 as an efficient and durable catalyst for dry reforming of methane

Facile Synthesis of Multi-Layered Nanostructured Ni/Ceo2 Catalyst Plus In-Situ Pre-Treatment for Efficient Dry Reforming of Methane

Engineering of Surface Properties of Ni-CeZrAl Catalysts for Dry Reforming of Methane

Enhanced activity and stability of Ce-doped PrCrO3-supported nickel catalyst for dry reforming of methane

CeO2 nanorod@NiPhy core‐shell catalyst for methane dry reforming: effect of simultaneous sintering prevention of CeO2 support and active Ni

Ni/Ce0.9Eu0.1O1.95 with enhanced coke resistance for dry reforming of methane

Rational design of nickel-based catalyst coupling with combined methane reforming to steadily produce syngas

Advancements in Methane Dry Reforming: Investigating Nickel–Zeolite Catalysts Enhanced by Promoter Integration

Enhanced Methane Dry Reforming with Ni/SiO2 Catalysts Featuring Hierarchical External Nanostructures

Ni-CeO2/SBA-15 Catalyst Prepared by Glycine-Assisted Impregnation Method for Low-Temperature Dry Reforming of Methane

Improving Catalytic Stability and Coke Resistance of Ni/Al2O3 Catalysts with Ce Promoter for Relatively Low Temperature Dry Reforming of Methane Reaction

Highly dispersed Ni/MgO-mSiO2 catalysts with excellent activity and stability for dry reforming of methane

CO2 Methanation on the Catalyst of Ni/MCM-41 Promoted with CeO2

Dry reforming of methane using cordierite monoliths with immobilized Ni–Ce catalysts

Highly active Ni/CeO2/SiO2 catalyst for low-temperature CO2 methanation: Synergistic effect of small Ni particles and optimal amount of CeO2