Abstract:This study was aimed to create strontium-calcium sulfate compounds for making a new bioactive material with osteoconductive and osteoinduceable activity for bone repairing. Its mechanics and degradation features were assessed in vitro. Powders of alpha-calcium sulfate hemihydrate (alpha-CSH) and SrCl2 were mixed completely to make Sr-calcium sulfate compounds materials with 6 different concentrations (0%, 0.1%, 0.3%, 0.5%, 1% and 2%) of Sr. Scanning electron microscope was used to observe the configuration of the new materials. The compressive strength of each material was tested. The materials were soaked into simulated body fluid (SBF) to test the features of degradation, which included pH, weight loss, declination of compressive strength and the changes of strontium ion concentration. The crystal appearances were influenced by incorporating of strontium. The compressive strength of non-strontium incorporating calcium sulfate was 36.65 +/- 2.22 MPa. When the concentration of strontium was increasing, the compressive strength measurements of the materials tended to decline. The compressive strength declined to 20.56 +/- 2.64 MPa when the strontium concentration reached to 2%. The pH value of the SBF declined when the time of degradation increased, but both of them were very stable. All of the materials got weight loss after being soaked in SBF for several weeks. The weight loss was slight within 4 weeks and it became dramatic after 4 weeks. When the concentration of strontium was increasing, the weight loss became more rapid and significant (P<0.05). During 0-4 weeks' degradation in SBF, the materials' compressive strength decreased much slower when the strontium concentration was below 0.5%; however, when the decrement of strength became faster, the strontium concentration became higher. The concentration of strontium ion in SBF began to increase faster after 4 weeks' soaking in SBF. As the concentration of strontium was increasing, the strontium ion concentration in SBF became higher (P = 0.000). The new compound materials made by the mixing of alpha-calcium sulfate hemihydrate and SrCl2 can provide efficient compressive strength. The features of degradation of the materials are very stable. The new materials can release lots of bone inducible substance-strontium ions to repair bone defection after 4 weeks of degradation.

Multi-stage controllable degradation of strontium-doped calcium sulfate hemihydrate-tricalcium phosphate microsphere composite as a substitute for osteoporotic bone defect repairing: degradation behavior and bone response

Controlled degradation of chitosan-coated strontium-doped calcium sulfate hemihydrate composite cement promotes bone defect repair in osteoporosis rats

3D Printing Magnesium-Doped Wollastonite/β-Tcp Bioceramics Scaffolds with High Strength and Adjustable Degradation

3D robocasting magnesium-doped wollastonite/TCP bioceramic scaffolds with improved bone regeneration capacity in critical sized calvarial defects

Cell-mediated degradation of strontium-doped calcium polyphosphate scaffold for bone tissue engineering.

Engineering Scaffolds Integrated with Calcium Sulfate and Oyster Shell for Enhanced Bone Tissue Regeneration

Strontium-substituted calcium sulfate hemihydrate/hydroxyapatite scaffold enhances bone regeneration by recruiting bone mesenchymal stromal cells

The Outstanding Mechanical Response and Bone Regeneration Capacity of Robocast Dilute Magnesium-Doped Wollastonite Scaffolds in Critical Size Bone Defects.

The Enhancement of Bone Regeneration by a Combination of Osteoconductivity and Osteostimulation Using Β-Casio3/β-ca3(po4)2 Composite Bioceramics.

Novel Bone Substitute Composed of Chitosan and Strontium-Doped Α-Calcium Sulfate Hemihydrate: Fabrication, Characterisation and Evaluation of Biocompatibility.

In Vivo Study of Porous Strontium-Doped Calcium Polyphosphate Scaffolds for Bone Substitute Applications

Strontium-substituted Biphasic Calcium Phosphate Microspheres Promoted Degradation Performance and Enhanced Bone Regeneration.

A novel calcium phosphate-based ceramic scaffolds with unexpected high osteogenic activity by strontium doping

Strontium Ranelate-Loaded POFC/β-TCP Porous Scaffolds for Osteoporotic Bone Repair

Preparation and Osteogenic Properties of Magnesium Calcium Phosphate Biocement Scaffolds for Bone Regeneration

A Bioceramic Scaffold Composed of Strontium-Doped Three-Dimensional Hydroxyapatite Whiskers for Enhanced Bone Regeneration in Osteoporotic Defects

A Multimaterial Scaffold With Tunable Properties: Toward Bone Tissue Repair

A Novel Bi-Phase Sr-doped Magnesium Phosphate/calcium Silicate Composite Scaffold and Its Osteogenesis Promoting Effect

[In Vitro Study of Strontium-Calcium Sulfate Compounds As Bioactive Bone Grafted Substitute].

3D-printed composite, calcium silicate ceramic doped with CaSO4·2H2O: Degradation performance and biocompatibility

Strontium hydroxyapatite/magnesium oxychloride cement with high strength and high osteogenic activity for bone defect repair