2D-Black Phosphorus/Polyaniline Hybrids for Efficient Supercapacitor and Hydrogen Evolution Reaction Applications

Namsheer K.,Samadhan Kapse,Mridula Manoj,Ranjit Thapa,Chandra Sekhar Rout,K. Namsheer

DOI: https://doi.org/10.1039/d2se00815g

2022-08-12

Abstract:With the emergence of wearable and portable electronics, solid-state supercapacitors are considered a promising candidate to power electronic devices because of their interesting features compared to existing energy storage devices. Polyaniline is a promising candidate for energy storage and conversion due to its high theoretical capacitance and intrinsic conductivity. Still, relatively sluggish rate capability and energy storage performance should be addressed to compete with existing high-performance electrode materials. Here we fabricated a solid-state supercapacitor electrode with an organic-inorganic of polyaniline (PANI) and black phosphorus (BP) to overcome the sluggish electrochemical performance. The fabricated supercapacitor device provides an exceptional specific capacitance of 969 mFcm-2 (323 Fg-1) at a current density of 0.4 mAcm-2 and displays a high energy density of 21.5 μWh/cm2 at a power density of 231 mW/cm2 along with good cycling stability of 83.3% after 10000 charge-discharge cycles. Also, this material shows a descent electrocatalytic HER performance with an overpotential value of 144 mV, a Tafel slope of 71 mV/dec, and outstanding stability up to 5.5 Hrs. Finally, DFT studies confirmed that the PANI/BP hybrid is a more promising electrode material for supercapacitor applications with higher CQ due to a larger density of states near the Fermi level as compared to pristine BP and PANI.

materials science, multidisciplinary,chemistry, physical,energy & fuels