A novel reed‐leaves like aluminum‐doped manganese oxide presetting sodium‐ion constructed by coprecipitation method for high electrochemical performance sodium‐ion battery

Kedi Cai,Xueqin Jing,Yuting Zhang,Lan Li,Xiaoshi Lang

DOI: https://doi.org/10.1002/er.8090

IF: 4.6

2022-05-24

International Journal of Energy Research

Abstract:A novel reed‐leaves like aluminum‐doped manganese oxide presetting sodium‐ion (NaxMnyAlzO2) is constructed by a facile coprecipitation method. It can be used as active material for sodium‐ion capacitor with 73.76 F g−1 of specific discharge capacity at 100 mA g−1 current density corresponding to 368.8 m2 g−1 electrochemical specific surface area. When combined with Na3V2(PO4)3 active materials it can bring about excellent electrochemical performances, which provide a new ideal for high‐performance sodium‐ion battery. Summary In this paper, Al‐doped manganese oxide with presetting sodium‐ion (NaxMnyAlzO2) is synthesized by a facile coprecipitation method and combines with Na3V2(PO4)3 cathode active materials for sodium‐ion battery in order to optimize the electrochemical performances. During the coprecipitation, a stable NaxMnyAlzO2 polynary metal oxide with Mn and Al molar ratio to 3:1 shows a special micromorphology similar to that of reed leaves, which makes it have a more ideal electrochemical specific surface area and ample mass transfer channels for rapid sodium‐ion insertion and desorption. Electrochemical test indicates that reed‐leaves like NaxMnyAlzO2 polynary metal oxides as active material for sodium‐ion capacitor exhibit a very excellent reversibility and low electrochemical (Rct = 434 Ω) and concentration polarization (DNa+ = 2.2728 × 10−11 cm2 s−1). Specific discharge capacity can achieve to 73.76 F g−1 at 100 mA g−1 current density corresponding to 368.8 m2 g−1 electrochemical specific surface area. After 200 cycles, the capacity retention rate can be maintained at 81.81%. In addition, reed‐leaves like NaxMnyAlzO2 polynary metal oxide playing a good depolarization role combined with Na3V2(PO4)3 active materials in the mass ratio to 7:3 can bring about the most excellent electrochemical performances.

energy & fuels,nuclear science & technology