Abstract:Solid-state electrolytes are key materials for developing high-safety solid-state Li-ion batteries. The garnet-type Li7La3Zr2O12 (LLZO) solid electrolyte is one of the most promising solid electrolytes due to its high conductivity and feasible preparation in ambient air. Among several dopants, Ta-doped LLZO (Ta-LLZO) delivers high stability against lithium metal and high conductivity, which attracts lots of researchers. However, production of Ta-LLZO ceramics is less problematic due to the complicated gas–liquid–solid sintering mechanism. This work aims to develop an efficient method to produce Ta-LLZO solid electrolyte ceramic pellets, including providing a stacking sintering method and optimizing the amount of excessive Li source, the wet milling duration, and the sintering temperature. First, a low-cost, efficient “gravel-separator” strategy is provided for multiple sintering of LLZO. Second, the Li6.5La3Zr1.5Ta0.5O12 (Ta5) samples with different excessive Li levels (2, 4, 6, and 8%) are sintered at various sintering conditions of 1240 °C for 60 min, 1280 °C for 20 min, and 1320 °C for 2 min to search for the optimum excessive amount of Li. Third, Ta5 samples with optimized excessive Li (4, 6%) after milling for longer duration are sintered at 1280 °C for 30 min, 1300 °C for 10 min, 1320 °C for 10 min, 1320 °C for 30 min to finally optimize the preparation craft. After optimization, the Ta5 ceramics with excessive 4 and 6% Li sintered at 1320 °C for 10 min deliver homogeneous and dense cross-sectional morphology, high conductivity of over 1 × 10–3 S cm–1 at room temperature, and relative densities of above 96%. Furthermore, symmetric Li cells assembled with the Ta-LLZO solid electrolyte prepared with the optimized method deliver a critical current density of 1.28 mA cm–2 at 30 °C and over 1000 h of stable cycling at 0.2 mA cm–2 (0.2 mA h cm–2) at 30 °C.

Li7La3Zr2O12-Based Solid Electrolytes Codoped with Ta5+ and Al3+ Ions for Lithium Power Sources

Enhancing the Ionic Conductivity and Stabilizing Cubic Structure of Garnet-Type Li6.25-xAl0.25La3Zr2-xTaxO12 by Al/Ta Co-Doping

Production of Ta-Doped Li 7 La 3 Zr 2 O 12 Solid Electrolyte with High Critical Current Density

Recent Strategies for Lithium-Ion Conductivity Improvement in Li7La3Zr2O12 Solid Electrolytes

Preparation and Electrochemical Properties of Zr-site Substituted Li7La3(Zr2−xMx)O12 (M = Ta, Nb) Solid Electrolytes

Preparation and electrochemical properties of LLZO co-doping with Al and Ti for all solid-state battery

Experimental and Computational Study of Mg and Ta‐Doped Li7La3Zr2O12 Garnet‐Type Solid Electrolytes for All‐Solid‐State Lithium Batteries

Al-doped Li7La3Zr2O12 garnet-type solid electrolytes for solid-state Li-Ion batteries

Co-doping strategy enhanced the ionic conductivity and excellent lithium stability of garnet-type Li7La3Zr2O12 electrolyte in all solid-state lithium batteries

Improvement of Ionic Conductivity in Li7La3Zr2O12 (LLZO) Solid Electrolyte By Doping with Aluminum/Tungsten

Stable Lithium-Ion Conducting Perovskite Lithium–strontium–tantalum–zirconium–oxide System

Rational Design of Strontium Antimony Co-Doped Li7La3Zr2O12 Electrolyte Membrane for Solid-State Lithium Batteries

Ga-doped lithium lanthanum zirconium oxide electrolyte for solid-state Li batteries

Probing Alkaline-Earth-Doped Garnet-Type Li 7 La 2.75 A 0.25 Zr 1.75 M 0.25 O 12 (A = Ca, Sr, Ba; M = Nb, Ta) Electrolytes for All-Solid-State Li Metal Batteries

Synergistically Engineering Grains and Grain Boundaries toward Li Dendrite-Free Li7La3Zr2O12

PVDF-HFP/LiTFSI based composite solid state electrolyte with different micromorphology of Li6.25Ga0.25La3Zr2O12 doping

The effect of a Ta, Sr co-doping strategy on physical and electrochemical properties of Li7La3Zr2O12 electrolytes

Optimizing Li+ Transport in Li7La3Zr2O12 Solid Electrolytes

The solid-state Li-ion conductor Li$_7$TaO$_6$: A combined computational and experimental study

Experimental and Computational Study of Mg and Ta‐Doped Li7La3Zr2O12 Garnet‐Type Solid Electrolytes for All‐Solid‐State Lithium Batteries (Adv. Sustainable Syst. 6/2024)

Enhancement in Li-ion Conductivity through Co-doping of Ge and Ta in Garnet Li$_7$La$_3$Zr$_2$O$_{12}$ Solid Electrolyte