Abstract:A simple activation method has been used to obtain porous carbon material from walnut shells. The effect of the activation duration at 400 °C in an atmosphere with limited air access on the structural, morphological, and electrochemical properties of the porous carbon material obtained from walnut shells has been studied. Moreover, the structure and morphology of the original and activated carbon samples have been characterized by SAXS, low-temperature adsorption porosimetry, SEM, and Raman spectroscopy. Therefore, the results indicate that increasing the duration of activation at a constant temperature results in a reduction in the thickness values of interplanar spacing (d002) in a range of 0.38–0.36 nm and lateral dimensions of the graphite crystallite from 3.79 to 2.52 nm. It has been demonstrated that thermal activation allows for an approximate doubling of the specific SBET surface area of the original carbon material and contributes to the development of its mesoporous structure, with a relative mesopore content of approximately 75–78% and an average pore diameter of about 5 nm. The fractal dimension of the obtained carbon materials was calculated using the Frenkel–Halsey–Hill method; it shows that its values for thermally activated samples (2.52, 2.69) are significantly higher than for the original sample (2.17). Thus, the porous carbon materials obtained were used to fabricate electrodes for electrochemical capacitors. Electrochemical investigations of these cells in a 6 M KOH aqueous electrolyte were conducted by cyclic voltammetry, galvanostatic charge/discharge, and impedance spectroscopy. Consequently, it was established that the carbon material activated at 400 °C for 2 h exhibits a specific capacity of approximately 110–130 F/g at a discharge current density ranging from 4 to 100 mA/g.

Effect of Synthesis Conditions on Capacitive Properties of Porous Carbon Derived from Hemp Bast Fiber

Correlation between structural properties and electrical conductivity of porous carbon derived from hemp bast fiber

Effect of Synthesis Conditions on Pseudocapacitance Properties of Nitrogen-Doped Porous Carbon Materials

Combined effect of nitrogen-doped functional groups and porosity of porous carbons on electrochemical performance of supercapacitors

Synthesis of Microporous Carbon Nanofibers and Nanotubes from Conjugated Polymer Network and Evaluation in Electrochemical Capacitor

Improving Supercapacitance of Electrospun Carbon Nanofibers through Increasing Micropores and Microporous Surface Area

Porous Cotton-derived Carbon: Synthesis, Microstructure and Supercapacitive Performance

Effect of Thermal Activation on the Structure and Electrochemical Properties of Carbon Material Obtained from Walnut Shells

Synthesis of multi-branched porous carbon nanofibers and their application in electrochemical double-layer capacitors

Investigating the effects of activating agent morphology on the porosity and related capacitance of nanoporous carbons

Microstructure and electrochemical properties of porous carbon derived from biomass

Nitrogen-doped carbon derived from composite of phenolic and amino foam: Effect of synthesis processes on physicochemical properties and super-capacitive performances

Charge Storage and Magnetic Properties Nitrogen-Containing Nanoporous Bio-Carbon

Effect of Porosity and Crystallinity of Activated Carbons for Electrochemical Capacitors

Capacitive properties of carbon nanofibers derived from blends of cellulose acetate and polyacrylonitrile

Effect of Pore Structure on the Electrochemical Performance of Coal-Based Activated Carbons in Non-Aqueous Electrolyte

The Effect of Pre-Carbonization of Mesophase Pitch-Based Activated Carbons on Their Electrochemical Performance for Electric Double-Layer Capacitors

Hydrothermal Activation of Porous Nitrogen-Doped Carbon Materials for Electrochemical Capacitors and Sodium-Ion Batteries

Functional Groups and Pore Size Distribution Do Matter to Hierarchically Porous Carbons as High-Rate-Performance Supercapacitors

Porous carbon fibers from gel-spun polyacrylonitrile and poly(methyl methacrylate)-block-poly(acrylonitrile)

Influence of Pore Structure of Coal-based Activated Carbons on Electric Double Layer Capacitance