First-principles study the mechanical, electronic, and thermodynamic properties of Mg-Al-Mn ternary compounds
Min Wang,Yunxuan Zhou,Wenjun Tian,Jianbo Li,Hongbing Chen,Jun Tan,Xianhua Chen
DOI: https://doi.org/10.1016/j.vacuum.2023.112140
IF: 4
2023-05-02
Vacuum
Abstract:In recent years, magnesium alloys have been used more and more widely due to their excellent lightweight and good plasticity. But correspondingly, the requirements for the elastic modulus ( E ) are more demanding. Therefore, to improve the deficiency, we are committed to find a way to increase the E . In this work, the mechanical, electronic, and thermodynamic properties of the Mg-Al-Mn ternary compounds were explored effectively based on first-principles calculations. It was found that the stabilities of these six structures were verified by the phonon spectrum, cohesive energy, and density of state, which showed that Mg 3 (MnAl 9 ) 2 possessed the best stability. Furthermore, Mg 3 (MnAl 9 ) 2 also had the largest bulk modulus, shear modulus, and E with values of 78.39, 50.94, and 125.6 GPa, respectively, due to the high bond strength of Al-Al bonds, and this was also verified by Mulliken's population analysis. Not only that, the largest hardness was reflected in Mg 3 (MnAl 9 ) 2 with a value of 9.04 and 9.11 GPa in Chen's and Tian's models. Similarly, the thermodynamic results showed that Mg 3 (MnAl 9 ) 2 had the highest Debye temperature as a value of 540.29 K and the highest limiting thermal conductivity with values of 1.216 W m −1 K −1 in Clarke's model and 0.945 W m −1 K −1 in Cahill's model.
materials science, multidisciplinary,physics, applied