Abstract:Ni nanoparticles supported on ZrO2 are a prototypical system for reforming catalysis converting methane to synthesis gas. Herein, we examine this catalyst on a fundamental level using a 2-fold approach employing industrial-grade catalysts as well as surface science based model catalysts. In both cases we examine the atomic (HRTEM/XRD/LEED) and electronic (XPS) structure, as well as the adsorption properties (FTIR/PM-IRAS), with emphasis on in situ/operando studies under atmospheric pressure conditions. For technological Ni-ZrO2 the rather large Ni nanoparticles (about 20 nm diameter) were evenly distributed over the monoclinic zirconia support. In situ FTIR spectroscopy and ex situ XRD revealed that even upon H2 exposure at 673 K no full reduction of the nickel surface was achieved. CO adsorbed reversibly on metallic and oxidic Ni sites but no CO dissociation was observed at room temperature, most likely because the Ni particle edges/steps comprised Ni oxide. CO desorption temperatures were in line with single crystal data, due to the large size of the nanoparticles. During methane dry reforming at 873 K carbon species were deposited on the Ni surface within the first 3 h but the CH4 and CO2 conversion hardly changed even during 24 h. Post reaction TEM and TPO suggest the formation of graphitic and whisker-type carbon that do not significantly block the Ni surface but rather physically block the tube reactor. Reverse water gas shift decreased the H2/CO ratio. Operando studies of methane steam reforming, simultaneously recording FTIR and MS data, detected activated CH4 (CH3 and CH2), activated water (OH), as well as different bidentate (bi)carbonate species, with the latter being involved in the water gas shift side reaction. Surface science Ni-ZrO2 model catalysts were prepared by first growing an ultrathin "trilayer" (O-Zr-O) ZrO2 support on an Pd3Zr alloy substrate, and subsequently depositing Ni, with the process being monitored by XPS and LEED. Apart from the trilayer oxide, there is a small fraction of ZrO2 clusters with more bulk-like properties. When CO was adsorbed on the (fully metallic) Ni particles at pressures up to 100 mbar, both PM-IRAS and XPS indicated CO dissociation around room temperature and blocking of the Ni surface by carbon (note that on the partially oxidized technological Ni particles, CO dissociation was absent). The Ni nanoparticles were stable up to 550 K but annealing to higher temperatures induced Ni migration through the ultrathin ZrO2 support into the Pd3Zr alloy. Both approaches have their benefits and limitations but enable us to address specific questions on a molecular level.

Zirconium Carbide Mediates Coke‐Resistant Methane Dry Reforming on Nickel‐Zirconium Catalysts

Nickel‐Catalyzed Dry Reforming of Methane Via Modulating the Zirconia Shapes

CO2 Methanation over Nickel-Based Catalysts Supported on MCM-41 with in Situ Doping of Zirconium

Surface Spectroscopy on UHV-Grown and Technological Ni-ZrO2 Reforming Catalysts: From UHV to Operando Conditions

A nanoscale Ni/ ZrO 2 catalyst coated with Al 2 O 3 for carbon dioxide reforming of methane

Carbon Dioxide Reforming of Methane Over Nanocomposite Ni/ZrO 2 Catalysts

Stable Ni/ZrO2 catalyst for carbon dioxide reforming of methane

Preparing a Zr-Doped CeO 2 Nanorod to Improve the Catalytic Performance of the Ni-Based Catalyst for Dry Reforming of Methane by Enhancing Oxygen Supply

Overcoming the kinetic and deactivation limitations of Ni catalyst by alloying it with Zn for the dry reforming of methane

Ni/Ce0.9Eu0.1O1.95 with enhanced coke resistance for dry reforming of methane

Highly Active and Stable Ni/ZrO2 Catalyst for Syngas Production by CO2 Reforming of Methane

Enhanced Dry Reforming of Methane Catalysis by Ni at Heterointerfaces between Thin MgAlOx and Bulk ZrO2

Unraveling the effects of Ce/Zr molar ratio in mesoporous CexZr1−xO2 on the performance of dry reforming of methane over the supported Ni catalysts

NixCoy Nanocatalyst Supported by ZrO2 Hollow Sphere for Dry Reforming of Methane: Synergetic Catalysis by Ni and Co in Alloy

Rationally constructing metastable ZrO 2 supported Ni catalysts for highly efficient and stable dry reforming of methane

Cs‐Promoted Co Particles on Yttria‐Stabilized Zirconia as Coke‐Tolerance Methane Dry Reforming Catalyst under Elevated Pressure

Synthesis of nickel catalysts supported on Zr-doped ordered mesoporous Al2O3 and their catalytic performance for low-temperature CO2 reforming of CH4

Combined Catalytic Partial Oxidation and CO2 Reforming of Methane over ZrO2-modified Ni/SiO2 Catalysts Using Fluidized-Bed Reactor

Promotional Effect of Ni−Sn Interaction over Ni Supported on Sn‐incorporated MCM‐41 Catalysts for CO 2 Reforming of CH 4

Insights on the Highly Stable and Coke-Resistant Nickel/Zirconia Nanocatalyst for the Methanation of Carbon Dioxide

Deciphering the ZrO2 phase engineering effects on dry reforming of methane over the Ni/ZrO2 catalysts