Influence of Hot Rolling on Microstructure, Corrosion and Mechanical Properties of Mg–Zn–Mn–Ca Alloy
Stanislav O. Rogachev,Viacheslav E. Bazhenov,Vasiliy A. Bautin,Anna V. Li,Sofia V. Plegunova,Denis V. Ten,Viacheslav V. Yushchuk,Alexander A. Komissarov,Kwang Seon Shin
DOI: https://doi.org/10.3390/met14111249
IF: 2.695
2024-11-05
Metals
Abstract:The effect of hot rolling on the microstructure, mechanical, and corrosion properties of the magnesium alloy 96 wt% Mg–2.3 wt% Zn–0.7 wt% Ca–1 wt% Mn was studied. After heat treatment, the original plates of an as-cast alloy were rolled from a 7 mm thickness to a 0.2 mm thickness at two temperatures—300 or 400 °C. It has been established that increasing the rolling temperature from 300 to 400 °C increases the fraction of recrystallized grains in the microstructure and after rolling at 400 °C, the microstructure is fully recrystallized. The best strength–ductility balance of the alloy was obtained after rolling at 300 °C, with a high total percentage reduction of 93–97%: the yield stress, the ultimate tensile strength, and the elongation averaged at 285 MPa, 310 MPa, and 5%, respectively. The alloy after rolling, annealed at 400 °C, shows improved ductility but lower strength: the yield stress, the ultimate tensile strength, and the elongation were 200 MPa, 260 MPa, and 17%, respectively. The strong dependence of corrosion resistance on respect to rolling direction is observed, which can be reduced after heat treatment. The as-rolled alloy and the heat-treated alloy had low corrosion rates in Hanks' solution of 0.54 and 0.19 mm/year, respectively.
materials science, multidisciplinary,metallurgy & metallurgical engineering