Abstract:The Nd-Fe-B anisotropic magnetic powders were subjected to tempering and ball milling processes. Analysis of the magnetic properties, structure, and physical phase revealed that the following: the integrated magnetic properties of the magnetic powder were the best when the tempering temperature and time were separately 650 °C and 20 min, for DOA = 0.73, B r = 6.547 kGs, H cj = 12.255 kOe, and ( BH ) max = 7.117 MGOe. When the DR temperature is 860 °C, the tempering temperature is 650 °C, and the tempering time is 20 min, the ideal magnetic properties of the magnetic powder are DOA = 0.69, B r = 6.238 kGs, H cj = 14.67 kOe, and ( BH ) max = 7.060 MGOe. The integrated magnetic properties of the magnetic powders were optimal when the ball milling speed, time, and doped Cu content were 350 rpm, 2 h, and 10 wt%, for DOA = 0.62, B r = 4.96 kGs, H cj = 9.86 kOe, and ( BH ) max = 4.39 MGOe. The ideal tempering temperature and time can promote the diffusion of Nd-rich phase to the grain boundaries, strengthen the pinning effect on the magnetic domains, and improve the coercivity of the magnetic powder. The ideal ball milling speed and time can effectively reduce the particle size of the main phase particles of the magnetic powder and the large particles of the Nd-rich phase, so that the Nd-rich phase is uniformly distributed at the grain boundaries, to achieve the effect of de-magnetization coupling and improve the coercivity of the magnetic powder. After ball milling the magnetic powder doped with an appropriate amount of Cu powder, Cu induces the precipitation of a certain amount of Nd in the main phase of Nd 2 Fe 14 B. This Nd is uniformly distributed at the grain boundaries, achieving the effect of repairing the grain boundaries, thereby improving the coercivity of the magnetic powder.

Effect of High Energy Ball Milling Washing Process on Properties of Nd2Fe14B Particles Obtained by Reduction-Diffusion

Morphology and magnetic properties of anisotropic Nd-Fe-B powders by surfactant-assisted ball milling

Study on the Influence of Annealing and Ball Milling on the Magnetic Properties of HDDR Nd-Fe-B Magnetic Powder

Mechanically activated disproportionation of NdFeB alloy by ball milling in hydrogen

Magnetic Property and Microstructure of Single Crystalline Nd2fe14b Ultrafine Particles Ball Milled from Hddr Powders

Preparation, Microstructure, and Magnetic Properties of A Nanocrystalline Nd12fe82b6 Alloy by Hddr Combined with Mechanical Milling

Research on efficiency of amorphous and nanocrystal line Nd2Fe14B/α-Fe powder prepared by two milling methods

Sol−Gel Based Chemical Synthesis of Nd2Fe14B Hard Magnetic Nanoparticles

Effects of milling and crystallization conditions on microstructure of Nd2Fe14B/α-Fe powder

Microstructure and magnetic properties of nanocomposite Nd2Fe14B/α-Fe magnetic material prepared by mechanical milling

Nd2Fe14B/α-Fe Nanocomposites Prepared by Mechanically Activated Disproportionation and Subsequent Desorption-Recombination

Hydriding/dehydriding properties of La2Mg16Ni alloy prepared by ball milling in different milling environments

Mechanical Ball Milling Preparation and Electrochemical Hydrogen Storage Properties of Amorphous Mg-Fe Composites

Microstructure and magnetic properties of nanocomposite Nd2Fe14B/α-Fe permanent magnetic powder prepared by mechanical milling

Preparation and microstructure features of nanocrystalline Nd12Fe82B6 alloy powder by a joint technique combining mechanical milling with HDDR

Effects of HDDR Treatment on Structure, Morphology and Particle Size of Nd-Fe-B Powders Prepared by Ball Milling of Nd-Fe-B Strip Cast Alloys

Effects of ball-milling time and Bi2O3 addition on electrochemical performance of ball-milled La2Mg17+200wt.% Ni composites

Permanent magnetic powder of nanocomposite Nd2Fe14B/α-Fe prepared by mechanical milling

Synthesis of nanopowders Nd 2Fe 14B by chemical method

Facile Synthesis of Nd2Fe14B Hard Magnetic Particles with Microwave-Assisted Hydrothermal Method

Chemical synthesis and coercivity enhancement of Nd2Fe14B nanostructures mediated by non-magnetic layer